ASTM A36 Steel, bar
Physical Properties | Metric | English | Comments |
Density  | 7.85 g/cc | 0.284 lb/in³ | |
  |
Mechanical Properties | Metric | English | Comments |
Tensile Strength,Ultimate  | 400 - 550 MPa | 58000 - 79800 psi | |
Tensile Strength, Yield  | 250 MPa | 36300 psi | |
Elongation at Break  | 20.0 % | 20.0 % | in 200 mm |
  | 23.0 % | 23.0 % | In 50 mm. |Modulus of Elasticity  | 200 GPa | 29000 ksi | |
Compressive Yield Strength  | 152 MPa | 22000 psi | Allowable compressive strength |
Bulk Modulus  | 140 GPa | 20300 ksi | Typical for steel |Poissons Ratio  | 0.260 | 0.260 | |
Shear Modulus  | 79.3 GPa | 11500 ksi | |
  |
Component Elements Properties | Metric | English | Comments |
Carbon, C  | 0.260 % | 0.260 % | |
Copper,Cu  | 0.20 % | 0.20 % | |
Iron, Fe  | 99.0 % | 99.0 % | |
Manganese, Mn  | 0.75 % | 0.75 % | |
Phosphorous, P  | <= 0.040 % | <= 0.040 % | |
Sulfur, S  | <= 0.050 % | <= 0.050 % ||

ASTM A36 Steel, flange
Physical Properties | Metric | English | Comments |
Density  | 7.85 g/cc | 0.284 lb/in³ | |
  |
Mechanical Properties | Metric | English | Comments |
TensileStrength, Ultimate  | 400 - 550 MPa | 58000 - 79800 psi | |
Tensile Strength, Yield  | 250 MPa | 36300 psi | |
Elongation at Break  | 20.0 % | 20.0 % | in 200 mm |
  | 21.0 % | 21.0 % | In 50mm. |
Modulus of Elasticity  | 200 GPa | 29000 ksi | |
Compressive Yield Strength  | 152 MPa | 22000 psi | Allowable compressive strength |
Bulk Modulus  | 140 GPa | 20300 ksi | Typical forsteel |
Poissons Ratio  | 0.260 | 0.260 | |
Shear Modulus  | 79.3 GPa | 11500 ksi | |
  |
Component Elements Properties | Metric | English | Comments |
Carbon, C  | <= 0.260 % | <=0.260 % | |
Copper, Cu  | 0.20 % | 0.20 % | |
Iron, Fe  | 98.0 % | 98.0 % | |
Manganese, Mn  | 1.10 % | 1.10 % | |
Phosphorous, P  | <= 0.040 % | <= 0.040 % | |
Silicon, Si  |...