degradacion de polietileno

Rev. peru. biol. 17(1): 133 - 136 (Abril 2010)
© Facultad de Ciencias Biológicas UNMSM

Biodegradación de polietileno de baja1727-9933
Versión Online ISSN densidad

Biodegradación de polietileno de baja densidad por acción de un
consorcio microbiano aislado de un relleno sanitario, Lima, Perú
Biodegradation of low density polyethylene by the action of a microbial
consortium isolated froma landfill, Lima, Peru
Diego Uribe, Daniel Giraldo, Susana Gutiérrez y Fernando Merino
Laboratorio de Microbiología y
Biotecnología Microbiana, Facultad
de Ciencias Biológicas, Universidad
Nacional Mayor de San Marcos.
Apartado 110058, Lima 11, Perú.
Email Diego Uribe:
diegour24@yahoo.com

Publicado impreso: 20/10/2010
Publicado online:
29/09/2010

En el presente trabajodescribimos el aislamiento y la actividad de biodegradación de microorganismos sobre
polietileno de baja densidad. Los microorganismos fueron aislados de materiales plásticos con evidencias de
deterioro procedentes de un relleno sanitario de Lima. Las muestras fueron filtradas y preseleccionadas en medio
de sales minerales a pH 5,5 y 7, para hongos y bacterias respectivamente. Se aislaron 6 cepas,identificadas
como Pseudomonas sp. MP3a y MP3b, Penicillium sp. MP3a, Rhodotorula sp. MP3b, Hyalodendron sp. MP3c
y una levadura no identificada. La acción degradativa del consorcio microbiano aislado fue evidenciada por
variaciones en el espectro infrarrojo del polietileno con respecto al polímero sin tratamiento, observándose la
reducción del índice de carbonilo (83,89% a pH 7 y 4,08% a pH 5,5)y de terminaciones con dobles enlaces
(19,77% a pH 7 y 6,47% a pH 5,5). Finalmente se determinó el porcentaje de peso perdido por el polietileno
sometido a las cepas aisladas, observándose una disminución de 5,4% a pH 7 y 4,8% a pH5,5.
Palabras claves: Espectroscopia, Polietileno, Plásticos, Biodegradación, Polímeros.

Abstract
In this paper, we describe the isolation and biodegradationactivity of microorganisms on low density polyethylene. The microorganisms were collected from plastic materials with evidence of deterioration from a landfill. The
samples were filtered and selected in a mineral salts medium at pH 5.5 and 7 for bacteria and fungi respectively.
Six strains were isolated, identified as Pseudomonas sp. Hyalodendron sp., Penicillium sp. and Rhodotorula sp.
Microbialactivity was evidenced by changes in the infrared spectrum of polyethylene with respect to the polymer
without treatment. Reduction of carbonyl index (83.89% at pH 7 and 4.08% at pH 5.5) and double bonds index
(19.77% at pH 7 and 6.47% at pH 5.5) were observed. Finally we determined the percentage of weight lost
by the polyethylene subjected to activity of the strains, with a decrease of 5.4% atpH 7 and 4.8% at pH5, 5.
Keywords: Spectroscopy, Polyethylene, Plastics, Biodegradation, Polymers.

Introducción
En la actualidad, los plásticos son productos muy utilizados y
fabricados en grandes cantidades; sin embargo, debido a su difícil
mineralización son uno de los contaminantes más importantes
de los suelos y océanos (Allsopp et al. 2007).
Las investigaciones frente al problema delos plásticos, están
dirigidas a la búsqueda de diferentes alternativas de reúso o degradación. Han sido producidos variantes de plásticos que contienen pro-oxidantes o polímeros biológicamente degradables,
y que permiten su completa mineralización (Burgess-Cassler et
al. 1991; Scott 1990; Johnson et al. 1993). En la actualidad,
adquieren especial importancia las investigaciones de bacterias,actinomicetos y hongos (Lee et al. 1990) que biodegradan de
manera óptima estos polímeros, o determinan las condiciones
que favorecerían esta acción en el medio ambiente (Bonhommea et al. 2003; Orhan et al. 2004). Por otro lado, se investigan
microorganismos capaces de sintetizar polímeros biodegradables
para crear nuevos plásticos (Martins & Marconato 2006), y microorganismos que producen...