HMS DESCRIPCION DE TIPOS DE CHATARRA

FICHA TECNICA / DATA SHEET

HMS 1 and HMS 2 scrap
It is the designation for recyclable steel and wrought Iron. HMS stands for 'Heavy
melting scrap'. HMS 2 contains galvanized and blackened steelwhereas HMS 1
doesn't.
HMS is 'Heavy Melting Scrap'. It is the generic term for most types of heavy steel
scrap, normally cut to a size not exceeding 1.5mx 0.5m. It consists of cut lengths ofpipe, re-bar, angles, steel poles, H or I beams, ships plate and so on. HMS 1 is the
term for heavier scrap which has a density of at least 0.7 tons per cubic meter,
whereas HMS 2 would be lighter steelscrap such as thin wall tubing (eg bicycle
frames), sheet scrap less than 3.2mm thick and so on. The two are normally sold
together with a ratio of 80/20 heavy and light. HMS is the descriptionused
worldwide, with Americans trading a similar type of scrap called ISRI grade 201. 201
is shorter (1m x 0.5m) and should be at least 6mm thick, making it a slightly superior
grade to HMS.Chatarra HMS 1 y 2
Es la designación para el acero reciclable y hierro forjado. El
HMS significa "chatarra pesada de fusión '. HMS 2 contiene acero galvanizado y
ennegrecido, mientras que el HMS 1 no.HMS es "fusión de chatarra pesada. Es el término genérico para la mayoría de los
tipos de chatarra de acero pesado, normalmente con corte a un tamaño que
no exceda de 1,5 mx 0,5 m. Se trata de laslongitudes de corte de tubos, barras de
nuevo, ángulos, postes de acero, vigas H o I, la placa de los buques y así
sucesivamente. HMS 1 es el término para la chatarra pesada que tiene una
densidad deal menos 0,7 toneladas por metro cúbico, mientras que el HMS 2 sería
chatarra de acero más ligera tal como tubos de pared delgada (por
ejemplo, cuadros de bicicleta), desechos de hoja de menos de3,2 mm de espesor y
así sucesivamente . Los dos se venden normalmente junto con una
proporción de 80/20. HMS es la descripción utilizada nivel mundial, el comercio con
los estadounidenses un tipo...