10 Autoguardado

10. cálculos.
-Compresión paralela.
Área transversal = (4.7)(4.7) = 22.09 cm2
Volumen = (22.09)(19.8) = 437.382 cm3
Densidad = Peso/volumen = 288.2/ 437.382 = 0.658 g/cm2
Deformación linealpromedio (e) = (0.050)+(0.180)+(0.010)+(0.030)/4
= 0.675 cm
Deformación unitaria (ε) = e/Lc = 0.6755/15 = 0.04503 cm/cm
Esfuerzo unitario (σ) = P/A = 1000/22.09 = 45.27 kg/cm2
-Compresión perpendicularÁrea transversal = (4.7)(4.7) = 22.09 cm2
Volumen = (22.09)(15.3) = 337.977 cm3
Densidad = Peso/volumen = (16.3)/( 337.977) = 0.0482 gr/cm3
Deformación lineal promedio (e) = (0.230)+(0.550)/2 = 0.39 cmDeformación unitaria (ε) =e/Lc = 0,39/15 = 0.026 cm/cm
Esfuerzo unitario (σ) = P/At = 200/22.09 = 9.053 kg/cm2
-Ensaye a flexión.
Área transversal = (4.6)(4.7) = 21.62cm2
Volumen = (21.62)(70.1) =1515.5562 cm3
Densidad = Peso/volumen = (1095)/(1515.5562) = 0.722 gr/cm3
Deflexión real (Δt) = 1.650/10 = 0.165 cm
Momento Flexionarte (M) = (P)(L)/4 = (50)(70.1)/4 = 876.25 kg cm
Deflexión real unitaria= (Δt)/(Lc) = (0.165)(70) = 0.002357 cm/cm
-Probeta de corte directo
Área transversal = (4.8)(4.7) = 22.56 cm2
Volumen = [(22.56)(1.4)]+[(3.1)(4.8)(6.2)] = 123.84 cm3
Densidad = Peso/volumen =64/123.84 = 0.516 gr/cm3



11. Registro de cálculos.
Ensaye de compresión paralelo.
Carga
DEFORMACION mm.
Deformación lineal promedio
Deformación unitaria
Esfuerzo unitario
Kg.
MIC.1
MIC. 2
MIC.3MIC.4



0
0
0
0
0
0
0
0
1000
0.050
0.180
0.010
0.030
0.0675
0.0045
45.26935265
2000
0.090
0.300
0.020
0.060
0.1175
0.007833333
90.5387053
3000
0.110
0.400
0.050
0.090
0.1625
0.010833333
135.8080579
40000.150
0.500
0.140
0.120
0.2275
0.015166667
181.0774106
5000
0.200
0.590
0.250
0.150
0.2975
0.019833333
226.3467632
6000
0.270
0.720
0.400
0.180
0.3925
0.026166667
271.6161159
7000
0.410
0.960
0.6300.220
0.555
0.037
316.8854685
7967
1.400
2.400
2.350
1.600
1.9375
0.129166667
360.6609325
Ensaye de compresión perpendicular
CARGA
DEFORMACION mm
Deformación lineal promedio
Deformación unitaria...