Aluminio 2117 t4

Aluminum 2117-T4
Categories: Metal; Nonferrous Metal; Aluminum Alloy; 2000 Series Aluminum Alloy Key Words: Aluminium 2117-T4; UNS A92117; AA2117-T4 Vendors: No vendors are listed for this material.Please click here if you are a supplier and would like information on how to add your listing to this material. Metric 2.75 g/cc Metric 70 93 81 300 MPa 165 MPa 27.0 %
@Thickness 1.60 mm

 Physical Properties Density    Mechanical Properties Hardness, Brinell  Hardness, Knoop  Hardness, Vickers  Tensile Strength, Ultimate  Tensile Strength, Yield  Elongation at Break  Modulus of Elasticity English 0.0994 lb/in³ English 70 93 81 43500 psi 23900 psi 27.0 %
@Thickness 0.0630 in

Comments Estimated from trends in similar Al alloys. Comments 500 kg load with 10 mm ball Converted fromBrinell Hardness Value Converted from Brinell Hardness Value

in 5 cm Average of Tension and Compression. In Aluminum alloys, the compressive modulus is typically 2% greater than the tensile modulus.Estimated from trends in similar Al alloys. Estimated from trends in similar Al alloys.

72.0 GPa

10400 ksi

Poissons Ratio  Fatigue Strength  Machinability  Shear Modulus  Shear Strength   Electrical Properties Electrical Resistivity    Thermal Properties CTE, linear   Specific Heat Capacity  Thermal Conductivity  Melting Point  Solidus  Liquidus    Component Elements PropertiesAluminum, Al  Chromium, Cr  Copper, Cu  Iron, Fe  Magnesium, Mg  Manganese, Mn  Silicon, Si  Zinc, Zn  References for this datasheet.  

0.330 95.0 MPa
@# of Cycles 5.00e+8

0.330 13800 psi
@# of Cycles5.00e+8

50 % 27.0 GPa 195 MPa Metric 0.00000430 ohm-cm Metric 23.8 µm/m-°C
@Temperature 20.0 - 100 °C

50 % 3920 ksi 28300 psi English 0.00000430 ohm-cm English 13.2 µin/in-°F
@Temperature 68.0- 212 °F

0-100 Scale of Aluminum Alloys Estimated from similar Al alloys.

Comments

Comments

25.6 µm/m-°C
@Temperature 20.0 - 300 °C

14.2 µin/in-°F
@Temperature 68.0 - 572 °F...