Caracterizacion de polimeros

Revista Iberoamericana de Polímeros García-Chavez y Mendoza Martínez

Volumen 11(2), Marzo de 2010 Propiedades morfológicas y reológicas de biopolímeros

ESTUDIO DE LAS PROPIEDADES MORFOLÓGICAS Y REOLÓGICAS DE UNA RED HÍBRIDA DE POLÍMEROS SINTETIZADA A PARTIR DE TRES BIOPOLÍMEROS: GELATINA/QUITOSAN/DEXTRAN Ricardo García Chávez1,2*, Ana María Mendoza Martínez1
1) Instituto Tecnológico deCiudad Madero, División de Estudios de Posgrado e Investigación (ITCM). Juventino Rosas y Jesús Urueta, Col. Los Mangos, Ciudad Madero, Tam., México, C.P. 89440, Tel/Fax. (833) 2 15 85 44. Correo electrónico: ricardo.garcia.chavez@gmail.com 2) Instituto Mexicano del Petróleo, Eje Central Lázaro Cárdenas Norte 152, San Bartolo Atepehuacan, Gustavo A. Madero, México, Distrito Federal. C.P. 07730Recibido: Junio de 2009; Aceptado: Enero de 2010
RESUMEN En este trabajo se preparó una red híbrida de polímeros (HPN) mediante síntesis simultánea a partir de tres biopolímeros: dextrano, quitosano y gelatina, disueltos en una solución de ácido acético. Estos fueron entrecruzados en presencia de glutaraldehído y posteriormente secados a -10 y 30ºC. Estos biopolímeros por separado, sonbiodegradables y no-tóxicos, por lo que han sido estudiados ampliamente para su uso en medicina. Estas características le permiten ser utilizados como soportes para el crecimiento de tejido conectivo sobre áreas gravemente dañadas por quemaduras en los humanos, así también, en algunos materiales como en el caso de liberadores graduales de fármacos por atrapamiento físico de antibióticos en la matrizpolimérica. Se obtuvieron materiales biopoliméricos a diferentes concentraciones de agente entrecruzante y método de secado (liofilización y horno de vacío), los cuales fueron caracterizadas mediante FTIR, SEM y DSC para evaluar sus propiedades morfológicas, térmicas, así como, su capacidad de absorción de agua. Palabras Claves: Red híbrida de polímeros, quitosano, gelatina, dextrano. ABSTRACT In thiswork a Hybrid Polymer Network (HPN) was prepared by simultaneous synthesis of three biopolymers: dextran, chitosan and gelatin dissolved in acetic acid solution, they were crosslinked in presence of glutaraldehyde being dried at -10 and 30ºC. These biopolymers separately are biodegradable and non toxic that they have been widely used for medical purposes. These characteristics let to be used bothas supports for connective tissue growing over areas severely damaged by burns in humans and in some materials as in the case of gradually drug release by physical trapping of antibiotics into the polymer matrix. Biopolymer materials were obtained at different concentrations of crosslinked concentrations and dryness method (freeze dry and vacuum oven) and were characterized by FTIR, SEM and DSCtechniques and rheological studies in order to evaluate their morphological, thermal and rheological properties in addition to their capacity to absorb water. Key words: Hybrid polymer network, Chitosan, Gelatin, Dextran.

INTRODUCCION Mientras que los usos originales de los polímeros en cirugía eran centrados primariamente en reposición de tejido conectivo, una multitud de nuevas aplicacioneshan emergido como resultado de amplios avances en las ciencias de biología molecular y biología desarrollada. El desarrollo de nuevas proteínas y drogas basadas en ácidos nucleicos los cuales no pueden ser tomados en la forma clásica de píldoras, proveen un nuevo impulso para el desarrollo de polímeros implantables que
88 Rev. Iberoam. Polím., 11(2), 88-109 (2010)

Revista Iberoamericana dePolímeros García-Chavez y Mendoza Martínez

Volumen 11(2), Marzo de 2010 Propiedades morfológicas y reológicas de biopolímeros

sirven como controladores y liberadores de drogas, así como las aplicaciones en campos relativamente nuevos como la ingeniería de tejidos, donde los polímeros son usados para asistir en la regeneración de tejidos tridimensionales y estructuras de órganos. Las redes...