Cerámica y Vidrio

Boletín de la Sociedad Española de Cerámica y Vidrio
Vol 50, 4, 201-206, Julio-Agosto 2011 ISSN 0366-3175. eISSN 2173-0431.
doi: 10.3989/cyv.262011

B O L E T I N D E L A S O C I E DA D E S PA Ñ O L A D E

Cerámica y Vidrio
A

R

T

I

C

U

L

O

Materiales vitrocerámicos del sistema MgO-Al2O3-SiO2
a partir de ceniza de cáscara de arroz
M.I. MARTÍN1, J.Ma. RINCÓN1, F.ANDREOLA2, L. BARBIERI2, F. BONDIOLI2, I. LANCELLOTTI2 y M. ROMERO1
Grupo de Materiales Vítreos y Cerámicos, Departamento de Construcción, Instituto de Ciencias de la Construcción Eduardo Torroja, IETcc-CSIC.
Serrano Galvache, 4, 28033, Madrid, España
2
Dipartimento di Ingegneria dei Materiali e dell’Ambiente. Università degli Studi di Modena e Reggio Emilia. Via Vignolese, 905, 41100, Modena,Italy

1

En este trabajo se muestran los resultados de un estudio de valorización de la ceniza de cáscara de arroz como materia prima
en la obtención de materiales vitrocerámicos. Se ha formulado un vidrio en el sistema base MgO-Al2O3-SiO2 incorporando
B2O3 y Na2O para facilitar los procesos de fusión y colado del vidrio. El vidrio se ha caracterizado mediante la determinación
de sucomposición química. Su comportamiento frente a la sinterización se ha llevado a cabo mediante Microscopía de
Calefacción (MC). La estabilidad térmica de las muestras y el mecanismo de cristalización preferente se ha estudiado mediante
Análisis Térmico Diferencial (ATD). La mineralogía de los materiales vitrocerámicos se ha llevado a cabo por Difracción de
rayos-X (DRX). Los resultados obtenidosmuestran que es posible utilizar ceniza de cáscara de arroz para producir materiales
vitrocerámicos mediante un proceso de sinterización seguido de cristalización, con nefelina (Na2O·Al2O3·2SiO2) como fase
cristalina mayoritaria en el intervalo de temperatura 700º-950ºC y forsterita (2MgO·SiO2) a temperaturas superiores a 950ºC.
Palabras Clave: ceniza de cáscara de arroz, vidrio, vitrocerámico,nefelina, forsterita
Glass-ceramic materials of system MgO-Al2O3-SiO2 from rice husk ash
This wok shows the results of a valorisation study to use rice husk ash as raw material to develop glass-ceramic materials.
An original glass has been formulated in the base system MgO-Al2O3-SiO2 with addition of B2O3 and Na2O to facilitate the
melting and poring processes. Glass characterization was carriedout by determining its chemical composition. Sintering
behaviour has been examined by Hot Stage Microscopy (HSM). Thermal stability and crystallization mechanism have been
studied by Differential Thermal Analysis (DTA). Mineralogy analyses of the glass-ceramic materials were carried out using
X-ray Diffraction (XRD). Results show that it is possible to use ash rice husk to produce glass-ceramicmaterials by a sintercrystallization process, with nepheline (Na2O·Al2O3·SiO2) as major crystalline phase in the temperature interval 700-950ºC
and forsterite (2MgO·SiO2) at temperatures above 950ºC.
Keywords: rice husk ask, glass, glass-ceramic, nepheline, forsterite
1. INTRODUCCIÓN
El desarrollo económico y social experimentado por el ser
humano a lo largo de su evolución ha estado asociadoa su
capacidad para explotar los recursos energéticos disponibles.
El modelo energético actual, basado en la utilización a gran
escala de combustibles fósiles (petróleo, carbón y gas), no
es sostenible, ya que presenta graves problemas asociados
al agotamiento de los recursos energéticos y al deterioro
medioambiental provocado por la utilización de estos
combustibles. Por tanto, esnecesario encontrar fuentes de
energía alternativas. En los últimos años se han desarrollado
diversos procesos eficientes para convertir la biomasa en
energía. Sin embargo, estos procesos no son completamente
“limpios” ya que en el proceso de combustión de la materia
orgánica se genera un residuo que es necesario tratar.
La ceniza de cáscara de arroz (CCA) es el residuo generado
en las plantas...