Propiedades en estado endurecido de concreto preparado con agua contaminada con cloruros
Omar Guzmán-González1, Herwing Z. López-Calvo 2, Víctor G. Jiménez-Quero3 y Pedro Montes-García3
1

Estudiante de la Maestría en Ciencias en Conservación y Aprovechamiento de Recursos Naturales, CIIDIR Unidad Oaxaca, IPN México.omar.ggon@gmail.com 2 Estudiante de Doctorado. Civil Engineering Faculty, University of New Brunswick, Canada 3 Profesor Investigador del Grupo de Materiales y Construcción del CIIDIR Unidad Oaxaca, IPN Hornos 1003 Sta. Cruz Xoxocotlán, C.P.71230, Oaxaca, México. Resumen

Se estudian propiedades en estado endurecido de concreto ordinario y de alto desempeño contaminado con cloruros. Para estepropósito, se elaboraron cuatro mezclas con y sin cloruros adicionados intencionalmente. Se determinó la resistencia a la compresión y módulo de elasticidad para cada mezcla en cilindros de 10x20 cm a los 28 días de edad. Los resultados mostraron que en el concreto ordinario contaminado con cloruros en un 3% del peso del cemento, las propiedades estudiadas no son significativamente afectadas cuando secompararon con aquellas de la mezcla no contaminada. Sin embargo, en la mezcla de concreto de alto desempeño elaborado con agua con cloruros se presentó una pérdida importante de trabajabilidad lo que indirectamente afectó sus propiedades en estado endurecido. Debido a esto, se observó una falta de adherencia entre la pasta-agregado, lo cual, influyó negativamente en la resistencia a la compresión enlas mezclas contaminadas con cloruros. El módulo de elasticidad del concreto de alto desempeño también sufrió una sensible disminución debido a los cloruros intencionalmente adicionados. Palabras clave: Ingreso de cloruro de sodio, resistencia a la compresión, módulo de elasticidad. Abstract The present work, the properties in hardened state of ordinary and high-performance concrete contaminatedwith chlorides were studied. For this purpose, four concrete mixtures with and without intentionally added chlorides were prepared. The 28-day compressive strength and modulus of elasticity of cylinders for each mixture were determined. The results showed that the compressive strength and modulus of elasticity of ordinary concrete were not significantly affected by the addition of chlorides in a 3%of the cement weight in its properties in hardened state compared to a mixture which was not contaminated. Nevertheless, in the mixture of high performance concrete elaborated with water with chlorides an important loss of the workability was experienced that indirectly affected its properties in hardened state. In this case, a lack of adhesion between the aggregate and the cement paste wasobserved, which negatively affected the compressive strength and the modulus of elasticity of the contaminated concrete. Keywords: sodium chloridepenetation, compressive strength, modulus of elasticity.

Introducción
El cemento ha contribuido al desarrollo de las civilizaciones, principalmente en la producción del concreto para el acrecentamiento de la infraestructura de los países, por lo que deunos años a la fecha se le ha denominado el ‘‘oro gris’’ (Obras, 2004). El agua, por otra parte, siendo un elemento vital para el desarrollo de las actividades empieza a escasear y el futuro es nada alentador por lo que se avecina lo que se denomina ‘‘la guerra por el agua’’, esto sugiere que las reservas de agua dulce se extinguirán, y se tendría que recurrir al uso de agua de mar. Lo anterior esrelevante debido a que hoy en día el concreto es sin duda uno de los materiales más utilizados en todo el mundo, y al parecer esta tendencia 35

continuará en los años venideros, principalmente en los países en desarrollo. El concreto es un conglomerado de ingredientes sólidos y agua que le dan propiedades de ingeniería y que el producto final depende principalmente de las características de...