ACI: VOL. 1(3), pp. 15-25 (2010)

Mahmud y otros

EFECTO DE LA TEXTURA DE ELECTRODEPÓSITOS DE ZINC EN ACERO
SOBRE SU RESISTENCIA A LA CORROSIÓN
THE TEXTURES OF ZINC ELECTRODEPOSITS ON STEEL AND THEIR EFFECT ON THE
CORROSION RESISTANCE
Zulema A. Mahmud1, Norma Míngolo2 y Gabriel Gordillo3
(1) INTI. Av. General Paz 5445, (1650) San Martín, Buenos Aires - Argentina
(2) CNEA. Av. GeneralPaz 1499, (1650) San Martín, Buenos Aires - Argentina
(3) Universidad de Buenos Aires, Facultad de Ciencias Exactas y Naturales, DQIAQF,
Cd. Universitaria. Pabellón 2, Buenos Aires – Argentina
(e-mail: zulema@inti.gob.ar)

Recibido: 05/07/2010 - Evaluado: 29/07/2010 - Aceptado: 16/08/2010

RESUMEN
En este trabajo, las texturas de depósitos de zinc en acero templado se correlacionan con laresistencia de
corrosión del metal base. Se estudian por difracción de rayos X las texturas de electrodepósitos de zinc. Los
depósitos de zinc se realizaron simulando las condiciones industriales de temperatura, tiempo y densidad de
corriente, utilizando soluciones de electrodeposición de ZnCl2 + NH4Cl en presencia y ausencia de tiourea. Según
se ha reportado, los depósitos de Zn con una altaintensidad en la textura de los planos basales (0,0,2) y bajas
intensidades en la textura de planos piramidales (del tipo (1,0,3), (1,1,2), (2,0,1)) presentan mayor resistencia a
la corrosión. Para tiempos de electrodeposición bajos, los cincados obtenidos desarrollan una textura (1,0,3) y
las densidades de corriente de corrosión son altas. Mientras que, para tiempos de deposición altos (10minutos),
los cincados tienen una textura (0,0,2) y el valor de la corriente de corrosión disminuye notablemente. La
preponderancia de la textura (0,2,2) en los planos basales y la baja intensidad de DRX para la textura (0,0,3)
en los planos piramidales, están asociados a los depósitos que presentan una alta resistencia a la corrosión.
ABSTRACT
In this work, textures of Zn deposits on mild steelare correlated with the corrosion resistance of the base metal.
Textures of electrodeposits chemically obtained were studied by using X-ray diffraction. Zinc deposits were
made simulating industrial conditions of temperature, time and current density, using electrodeposition solutions
of ZnCl2 + NH4Cl (in the presence/absence of thiourea). According to reports, Zn deposits with a basal planeshigh intensity (0,0,2) and low intensities in pyramidal planes ((1,0,3), (1,1,2), (2,0,1)), more resistant to
corrosion . For low electrodeposition times, zinc deposits developed a (1,0,3) texture, showing in this case high
corrosion current densities. On the contrary, for higher deposition times (10 minutes), deposits developed a
(0,0,2) texture and the value of the corrosion current decreasesmarkedly. The prevalence of texture (0,0,2) in
the basal planes and low XRD intensity for (0,0,3) texture in the pyramidal planes are associated to deposits
having high corrosion resistance.
Palabras clave: electrodepósito, zinc, textura, resistencia a la corrosión
Keywords: electrodeposits, zinc, texture, corrosion resistance

AVANCES EN CIENCIAS E INGENIERÍA (ISSN: 0718-8706)

15ACI: VOL. 1(3), pp. 15-25 (2010)

Mahmud y otros

INTRODUCCIÓN
Las experiencias de electrodeposición se realizaron mediante transientes galvanostáticos (Milchev y Montenegro,
1992; Milchev, 1998a; Milchev, 1998b; Fletcher 1978; Fletcher, 2002), aplicando una corriente de acuerdo a un
procedimiento de tipo industrial. Según sea el transiente durante la deposición se puede inferir cómo es laevolución del potencial en la muestra.
Es fundamental mantener tanto la corriente como el potencial estacionario en la muestra durante el tiempo de la
experiencia y asegurar que no se aplique una corriente tan alta durante la electrodeposición de manera tal que
la evolución sea a un valor tan alto del potencial, en el que ocurra otra reacción aparte de la reducción del Zn2+,
como puede ser la...