ensayo lamina aluminio

Revista Latinoamericana de Metalurgia y Materiales 2009; 29 (2): 128-134

ESTIMACIÓN VÍA EXPERIMENTAL DE LA FORMABILIDAD DE LÁMINAS DE
ALUMINIO DE PUREZA COMERCIAL
Jhon E. Barbosa 1*, Ismael H. García 1, José J. Fuentes 2*
1: Universidad Francisco de Paula Santander, Grupo de Investigación Diseño Mecánico y Mantenimiento, Avda. Gran
Colombia, Nº 12E-96, Apdo. 1055, Cúcuta, Colombia.
2:Universidad Nacional Experimental del Táchira, Dpto. Ing. Mecánica, Avda. Universidad, s/n, Apdo. 436, San
Cristóbal, Venezuela.
*E-mail: jhebar@hotmail.com; jfuentes@unet.edu.ve
Recibido: Nov-2008; Revisado: 22-Jul-2009; Aceptado: 23-Jul-2009
Publicado On-Line: 21-Dic-2009
Disponible en: www.rlmm.mt.usb.ve
Trabajo presentado en el congreso “X Iberoamericano de Metalurgia y Materiales (X IBEROMET)”celebrado en Cartagena, Colombia,
del 13 al 17 de Octubre de 2008; y seleccionado para ser remitido a la RLMM para su arbitraje reglamentario y publicación.

Resumen
En este trabajo se investigó por vía experimental la formabilidad de láminas de aluminio de pureza comercial
designado AA-1100-O de 0,6 y 0,7 mm de espesor. Se trabajó con muestras de láminas, tal y como son fabricadas,
efectuándosele alas mismas estudios de laboratorio tales como: análisis químico, ensayo de tracción, ensayo de altura de
copa y ensayo con punzón hemisférico. De esta manera, se determinaron la resistencia a la tracción, el límite elástico
convencional, el porcentaje de alargamiento hasta fractura, el coeficiente de endurecimiento por deformación, la altura de
copa y la curva límite de formado; factores todos queayudan a pronosticar la formabilidad de la lámina. En concreto, se
encontró que la facilidad de conformación mecánica de la lámina mejora con el aumento de su espesor. Asimismo, se
determinó que existe una correlación apropiada entre la formabilidad, el espesor, el porcentaje de alargamiento hasta
fractura en tracción, la altura de copa y las curvas límites de formado.
Palabras Claves:Formabilidad, Altura de Copa, Curva límite de formado.
Abstract
This paper presents an experimental study of the formability of commercially pure aluminum sheets, with 0.6 and
0.7 mm thickness, designated AA-1100-O. In this research several laboratory tests were conducted, such as: chemical
analysis, tensile test, ball punch deformation test and hemispherical punch method. The tested parameters with directo
indirect influence in the aluminum sheet formability were: ultimate tensile strength, yield strength, total elongation, the
strain hardening exponent, cup height and forming limit diagrams, which were determined by testing samples cut from the
sheet, as received. The results of these tests allowed to establish that the aluminum sheet formability increased with
thickness. In addition, goodcorrelations were obtained between formability, thickness, total elongation, cup height and
forming limit diagrams.
Keywords: Formability, Cup height, Forming limit curve.

1. INTRODUCCIÓN
La tecnología de conformación mecánica de la
lámina metálica –p.ej., embutido profundo,
estirado– tiene especial importancia en la
fabricación de componentes estructurales en la
industria del automóvil, aeronáuticay otros sectores
[1]. Los metales más usados para tal propósito son
aceros, aleaciones de aluminio y aleaciones de
titanio [2]. El éxito de dicha tecnología depende de
la formabilidad de la lámina, que está relacionada
con la optimización y control de calidad del
producto final [3]. La formabilidad puede definirse
128

como una medida de la cantidad de deformación que
un material puedeexperimentar en un proceso de
formado sin que falle, tal como adelgazamiento
localizado o fractura [4]. La formabilidad varía con
las propiedades del material y las condiciones de
deformación [5]. Por otra lado, el campo de
esfuerzos y deformaciones son tan diversos durante
un proceso de formado que un sólo ensayo no sirve
para predecir la formabilidad de los materiales en
todas las situaciones [6].
La...