Fibra De Carbono
Páginas: 9 (2239 palabras)
Publicado: 25 de mayo de 2012
|FIBRA DE CARBONO
Abstract
Carbon fiber (carbon fibre), alternatively graphite fiber, carbon graphite or CF, is a material consisting of extremely thin fibers about 0.005–0.010 mm in diameter and composed mostly of carbon atoms. The carbon atoms are bonded together in microscopic crystals that are more or less alignedparallel to the long axis of the fiber. The crystal alignment makes the fiber very strong for its size. Several thousand carbon fibers are twisted together to form a yarn, which may be used by itself or woven into a fabric. Carbon fiber has many different weave patterns and can be combined with a plastic resin and wound or molded to form composite materials such as carbon fiber reinforced plastic (alsoreferenced as carbon fiber) to provide a high strength-to-weight ratio material. The density of carbon fiber is also considerably lower than the density of steel, making it ideal for applications requiring low weight. The properties of carbon fiber such as high tensile strength, low weight, and low thermal expansion make it very popular in aerospace, civil engineering, military, and motorsports,along with other competition sports. However, it is relatively expensive when compared to similar materials such as fiberglass or plastic. Carbon fiber is very strong when stretched or bent, but weak when compressed or exposed to high shock (e.g. a carbon fiber bar is extremely difficult to bend, but will crack easily if hit with a hammer).
Keywords
Metonimia, termoestables, viniléster,poliacrialonitrilo, catalizador, diglicidileter de bisfenol, pandeo, grafitización, alótropo, utillaje.
Definición
La fibra de carbono es un material compuesto, constituido principalmente por carbono. Tiene propiedades mecánicas similares al acero y es tan ligera como la madera o el plástico. Por su dureza tiene menor resistencia al impacto que el acero. Al igual que la fibra de vidrio, es uncaso común de metonimia, en el cual se le da al todo el nombre de una parte, en este caso el nombre de las fibras que lo refuerzan.
Al tratarse de un material compuesto, en la mayoría de los casos -aproximadamente un 75%- se utilizan polímeros termoestables. El polímero es habitualmente resina epoxi, de tipo termoestable aunque otros polímeros, como el poliéster o el viniléster también se usan comobase para la fibra de carbono aunque están cayendo en desuso.
La fibra de carbono es el desarrollo más reciente en el campo de los materiales compuestos siguiendo la idea de que uniendo fibras sintéticas con varias resinas, se pueden lograr materiales de baja densidad, muy resistentes y duraderos.
En el caso particular de la fibra de carbono, básicamente se combina un tejido de hilos decarbono (refuerzo), el cual aporta flexibilidad y resistencia, con una resina termoestable (matriz), comúnmente de tipo epoxi, que se solidifica gracias a un agente endurecedor y actúa uniendo las fibras, protegiéndolas y transfiriendo la carga por todo el material; por su parte el agente de curado ayuda a convertir la resina en un plástico duro.
De la combinación de estos tres componentes, seobtienen las propiedades mecánicas del nuevo material, pues aunque la malla de hilos de carbono, constituye por sí sola un elemento resistente, necesita combinarse con la resina para que la proteja de factores externos y esfuerzos físicos.
[pic]
Entre 5 y 10 micras mide un
filamento de carbono, cinco
veces más delgado que un
cabello humano.
Tejido de carbono
El tejido de fibrasde carbono procede de una mezcla de polímeros, el más utilizado es el PAN (poliacrilonitrilo) que por ser la materia prima se llama precursor y que normalmente se combina con otros polímeros: metil acrilato, metil metacrilato, vinil acetato y cloruro de vinilo, todos derivados del petróleo, que es carbono concentrado, proveniente de restos de materia orgánica (fósiles).
En particular, el PAN...
Abstract
Carbon fiber (carbon fibre), alternatively graphite fiber, carbon graphite or CF, is a material consisting of extremely thin fibers about 0.005–0.010 mm in diameter and composed mostly of carbon atoms. The carbon atoms are bonded together in microscopic crystals that are more or less alignedparallel to the long axis of the fiber. The crystal alignment makes the fiber very strong for its size. Several thousand carbon fibers are twisted together to form a yarn, which may be used by itself or woven into a fabric. Carbon fiber has many different weave patterns and can be combined with a plastic resin and wound or molded to form composite materials such as carbon fiber reinforced plastic (alsoreferenced as carbon fiber) to provide a high strength-to-weight ratio material. The density of carbon fiber is also considerably lower than the density of steel, making it ideal for applications requiring low weight. The properties of carbon fiber such as high tensile strength, low weight, and low thermal expansion make it very popular in aerospace, civil engineering, military, and motorsports,along with other competition sports. However, it is relatively expensive when compared to similar materials such as fiberglass or plastic. Carbon fiber is very strong when stretched or bent, but weak when compressed or exposed to high shock (e.g. a carbon fiber bar is extremely difficult to bend, but will crack easily if hit with a hammer).
Keywords
Metonimia, termoestables, viniléster,poliacrialonitrilo, catalizador, diglicidileter de bisfenol, pandeo, grafitización, alótropo, utillaje.
Definición
La fibra de carbono es un material compuesto, constituido principalmente por carbono. Tiene propiedades mecánicas similares al acero y es tan ligera como la madera o el plástico. Por su dureza tiene menor resistencia al impacto que el acero. Al igual que la fibra de vidrio, es uncaso común de metonimia, en el cual se le da al todo el nombre de una parte, en este caso el nombre de las fibras que lo refuerzan.
Al tratarse de un material compuesto, en la mayoría de los casos -aproximadamente un 75%- se utilizan polímeros termoestables. El polímero es habitualmente resina epoxi, de tipo termoestable aunque otros polímeros, como el poliéster o el viniléster también se usan comobase para la fibra de carbono aunque están cayendo en desuso.
La fibra de carbono es el desarrollo más reciente en el campo de los materiales compuestos siguiendo la idea de que uniendo fibras sintéticas con varias resinas, se pueden lograr materiales de baja densidad, muy resistentes y duraderos.
En el caso particular de la fibra de carbono, básicamente se combina un tejido de hilos decarbono (refuerzo), el cual aporta flexibilidad y resistencia, con una resina termoestable (matriz), comúnmente de tipo epoxi, que se solidifica gracias a un agente endurecedor y actúa uniendo las fibras, protegiéndolas y transfiriendo la carga por todo el material; por su parte el agente de curado ayuda a convertir la resina en un plástico duro.
De la combinación de estos tres componentes, seobtienen las propiedades mecánicas del nuevo material, pues aunque la malla de hilos de carbono, constituye por sí sola un elemento resistente, necesita combinarse con la resina para que la proteja de factores externos y esfuerzos físicos.
[pic]
Entre 5 y 10 micras mide un
filamento de carbono, cinco
veces más delgado que un
cabello humano.
Tejido de carbono
El tejido de fibrasde carbono procede de una mezcla de polímeros, el más utilizado es el PAN (poliacrilonitrilo) que por ser la materia prima se llama precursor y que normalmente se combina con otros polímeros: metil acrilato, metil metacrilato, vinil acetato y cloruro de vinilo, todos derivados del petróleo, que es carbono concentrado, proveniente de restos de materia orgánica (fósiles).
En particular, el PAN...