ingeniero mecanico

Avances en Ciencias e Ingeniería - ISSN: 0718-8706
Av. cien. ing.: 4(2), 43-50 (Abril/Junio, 2013)

Refugio-García et al.

MICRODUREZA DE LA SUPERALEACIÓN NICKELVAC (N-90)
MANUFACTURADA POR PULVIMETALURGIA
MICROHARDNESS OF THE NICKELVAC SUPERALLOY (N-90) MANUFACTURED BY
POWDER METALLURGY
Elizabeth Refugio-García1, José G. Miranda-Hernández2, Noé Velázquez-Barrón3,
José A.Rodríguez-García3, Enrique Rocha-Rangel3
(1) Universidad Autónoma Metropolitana, Departamento de Materiales, Av. San Pablo No. 180,
Col. Reynosa-Tamaulipas, 02200 México, D.F. - México
(2) Universidad Autónoma del Estado de México (UAEM-Valle de México), IIN, Blvd. Universitario S/N,
Predio San Javier, 54500 Atizapán de Zaragoza - México
(3) Universidad Politécnica de Victoria, Av. Nuevas Tecnologías5902, Parque Científico y Tecnológico de
Tamaulipas, 87138 Ciudad Victoria, Tamaulipas - México
(e-mail: erochar@upv.edu.mx)

Recibido: 12/09/2012 - Evaluado: 15/11/2012 - Aceptado: 27/12/2012

RESUMEN
A través de la técnica de metalurgia de polvos se fabricó la aleación denominada comercialmente como
nickelvac (N-90), que se trata de una superaleación hecha principalmente a base de níquel.La aleación
fabricada fue sometida primeramente a un proceso de homogenizado a dos temperaturas distintas (1000 y
1065°C durante 2 h) y posteriormente fue envejecida a 350°C durante diferentes tiempos (0.5, 1, 2 y 3 h). De
las mediciones de microdureza realizadas en las diferentes muestras, se obtuvo que mayores tiempos de
envejecido reflejan mayores valores de dureza. De las observaciones dela microestructura con ayuda de
microscopía electrónica de barrido, se pudo determinar la formación de precipitados del tipo Ni xTiy, siendo estos
los causantes de los incrementos en la dureza de la aleación, estos precipitados tienen su origen durante el
envejecido de la aleación.
ABSTRACT
Through powder metallurgy it was fabricated the nickelvac alloy, which is a superalloy mainly made bynickel.
The fabricated alloy was homogenized at two different temperatures (1000 and 1065 °C during 2h) and later
aged at 350°C during different times (0.5, 1, 2, and 3 h). From microhardness measurements realized in the
samples, it was determined that the more time of aged meet, the more hardness reflected. From microstructure
observations made by scanning electron microscopy, it wasdetermined the formation of NixTiy-type
precipitates, being these responsible for the microhardness improvement of the made alloy, these precipitates
have their origin during the alloy aged.
Palabras clave: microdureza; superaleación; níquel; metalurgia de polvos
Keywords: microhardness; superalloy; nickel; powder metallurgy

http://www.exeedu.com/publishing.cl/av_cienc_ing/

43

Avances enCiencias e Ingeniería - ISSN: 0718-8706
Av. cien. ing.: 4(2), 43-50 (Abril/Junio, 2013)

Refugio-García et al.

INTRODUCCIÓN
Las superaleaciones son aleaciones metálicas que contienen grandes cantidades de diferentes elementos
metálicos, las cuales se conciben con la idea de obtener un metal que presente la combinación de alta
resistencia mecánica y a la corrosión a elevadas temperaturastal y como lo explica Reed (2006). Dentro de
estos nuevos materiales, se encuentran las superaleaciones de níquel mismas que presentan un buen
comportamiento mecánico a temperaturas cercanas a los 1000°C según lo han establecido Bhadeshia (2003) y
Blaine et al. (2010). Estas aleaciones presentan una microestructura muy peculiar, y se ha documentado (ASM
Specialty Handbook, 2000) que es lacausante de sus excelentes propiedades mecánicas, en esta
microestructura se tiene presente una distribución en dos fases llamadas; gamma (γ) y gamma prima (γ´). La
fase gamma es una solución sólida centrada en las caras que actúa como matriz, mientras que la fase gamma
prima es una dispersión de precipitados ordenados del tipo intermetálico, y son responsables de la gran
resistencia de las...