Lixiviacion De Minerales Mangano-Argentiferos

DISOLUCIÓN DE VALORES DE ORO Y PLATA DE MINERALES MANGANO-ARGENTÍFEROS
G.T. MUNIVE1, A. L. LEAL-CRUZ 1, M. A. ENCINAS-ROMERO 1, J. H. CORONADO-LÓPEZ1, L. A. ALMAZÁN-HOLGUIN y F. BROWNBOJÓRQUEZ 2 1 Departamento de Ingeniería Química y Metalurgia y 2 Departamento de Investigación en Polímeros y Materiales, Universidad de Sonora. Rosales y Blvd. Luis Encinas S/N, Hermosillo, Sonora, 83000, México.gtmunive@iq.uson.mx RESUMEN Los estados de Puebla, Coahuila, Zacatecas, Jalisco y Sonora en México, cuentan con grandes yacimientos manganoargentíferos con contenidos relativamente altos de manganeso (2-12 % en peso) y con valores económicos de plata de 150-500 g/ton. Actualmente, muchos de estos minerales no pueden ser procesados por cianuración, debido a las características refractariasinherentes a la asociación plata-manganeso, que impiden la disolución de la plata. Por ello, se requiere de procesos viables para beneficiarlos eficientemente. En esta investigación, se propone un proceso combinado y fundamentado en la disolución inicial de manganeso bajo condiciones reductoras, seguido por la lixiviación de oro y plata con tiosulfato de sodio compuesto. Antes de la lixiviación, elmineral se somete a un pretratamiento con agentes reductores de manganeso (ácido sulfúrico, cloruro de sodio, carboximetilcelulosa, dióxido de azufre y sulfito de sodio). Para estudiar la velocidad de disolución de oro y plata, se consideraron las siguientes variables: tiempo de lixiviación, tipo de agente reductor, concentración del agente lixiviante y tamaño de partícula. Las técnicas de análisisutilizadas fueron: difracción rayos X, microscopia electrónica de barrido y análisis químico por vía húmeda. El proceso propuesto es una alternativa viable para el tratamiento de menas con alto contenido de manganeso. Palabras Clave: Minerales Refractarios, Lixiviación, Tiosulfato, Cianuro.

DISSOLUTION OF GOLD AND SILVER FROM ARGENTIFEROUS MANGANESE ORES
ABSTRACT The States of Puebla, Coahuila,Zacatecas, Jalisco, and Sonora in México, have a great amount of argentiferous-manganese ore deposits, with high values of manganese (2-12 wt.%) and silver (150 to 500 g/ton). Unfortunately, these ores cannot be processed by leaching with cyanide, due to its refractory nature attributed to the silver-manganese association, which impedes the silver dissolution. Because of this, the development ofviable processing

technologies to benefit this kind of refractory ores is required. In the present research, a novel process is considered for the treatment of ores containing high manganese values. The process is based in a pretreatment to reduce manganese with chemical agents (sulfuric acid, sodium chloride, carboxymethylcellulose, sulfur dioxide, and sodium sulfite), followed by a leachingprocess with stabilized sodium thiosulfate. With the purpose of study the dissolution rate of gold and silver in pretreated ores with stabilized sodium thiosulfate, the leaching parameters were varied, as follows: leaching time, kind of reducing agents, concentration of leaching agent and particle size. Samples were analyzed by X-ray diffraction, scanning electron microscopy and chemical analysistechniques. According to these results, the process with pretreatment of manganese and leaching with stabilized sodium thiosulfate is a viable alternative for the treatment of argentiferous-manganese ores. Keywords: Refractory Ores, Leaching, Thiosulfate, Cyanide. INTRODUCCIÓN La mayor parte de los minerales de oro y plata con altos contenidos de manganeso, no pueden ser procesados por cianuración.Esto se debe a las características refractarias inherentes a la asociación plata-manganeso, que impiden la disolución de la plata. Actualmente, México cuenta con importantes yacimientos de minerales refractarios con alto contenido de manganeso y valores importantes de oro y plata, los cuales no son explotados (Figura 1).

Figura 1. Minas manganeso y plata En la Figura 1, se presentan los...