Normal

EFECTO DE LAS CONDICIONES DE CURADO DEL HORMIGÓN EN SU COMPORTAMIENTO FRENTE A LOS CICLOS HIELO-DESHIELO Ghaida Al-Assadi1, María Jesús Casati2, Jaime Fernández1, Jaime C. Gálvez1
1

Departamento de Ingeniería Civil: Construcción, E.T.S. de Ingenieros de Caminos, Canales y Puertos, Universidad Politécnica de Madrid, C/ Profesor Aranguren s/n, 28040 Madrid, España E-mail: ghaida@caminos.upm.es;jfernandez@intemac.es; jcgalvez@caminos.upm.es
2

Departamento de Vehículos Aeroespaciales, E.U.I.T. Aeronáutica, Pl. Cardenal Cisneros s/n, 28040 Madrid, España. E-mail: mariajesus.casati@upm.es RESUMEN

El objetivo de este trabajo es relacionar las condiciones de curado del hormigón y la adición de un inclusor de aire, con los daños producidos por los ciclos hielo-deshielo en hormigonescurados con baja humedad y alta temperatura. Para ello se ha realizado una campaña experimental sobre probetas de hormigón curadas en condiciones extremas reales “in situ” de humedad y temperatura con y sin aire ocluido sometida a ciclo de hielo deshielo. El trabajo presenta la correlación de la evaluación del comportamiento mecánico del hormigón sometido a ciclos hielo-deshielo frente al grado dehidratación del hormigón y el volumen y tamaños de los poros. De los resultados obtenidos se concluye que las probetas sin aireante muestran un deterioro de sus propiedades mecánicas tras el ensayo de hielo-deshielo. Sin embargo, la inclusión de aire beneficia el comportamiento del hormigón frente a los ciclos hielo-deshielo, de modo que incluso mejoran sus propiedades mecánicas tras el ensayo.Este comportamiento anómalo se explica porque el proceso de hidratación del cemento continúa durante los ensayos hielo-deshielo, cerrando la red porosa. Este aspecto se ha podido confirmar con los ensayos de ATD y TG realizados.

ABSTRACT The main objective of this is to analyze the simultaneous potential damage of concrete specimens exposed to different curing conditions (high temperature and lowrelative humidity) and freeze-thaw cycles. This experimental campaign was realized on concrete specimen cured in real extreme conditions of humidity and temperature of 30°C and 37 % relative humidity, and with and without air-entraining admixtures subjected to freeze-thaw cycles. Concretes with characteristics strength of 30 y 45MPa, with and without air- entraining admixtures (AEA), weresubjected to two different curing conditions: wet and air dried conditions. In addition to the freezing- thawing test, additional durability tests were performed including: mercury intrusion porosimetry, the differential thermal analysis (ATD), termogravimetric analysis (TG). From the obtained results, it can be concluded that the specimens without airentraining experienced deterioration in theirmechanical properties as a result of the freeze-thaw test. The inclusion of air benefited the behaviour of concrete against the freeze-thaw cycles, to the extent that some of the specimens experienced an improvement in their mechanical properties after the freeze-thaw testing. The pore volume and size seems to be higher in the specimens before exposure to the freeze-thaw cycles. These results areattributed to the fact that the hydration process of the cement continued during the freeze-thaw cycles. PALABRAS CLAVE: Hormigón, ciclos hielo-deshielo, hidratación, porosidad, curado. movimientos moderados pueden considerarse en el diseño. Sin embargo, surgen problemas de durabilidad cuando el hormigón húmedo en climas fríos está expuesto a los ciclos repetidos de temperatura que causan el hielo y eldeshielo del agua de los poros. La expansión del hormigón húmedo puede ser alta y las tensiones inducidas dentro del hormigón pueden ser inaceptables.

1. INTRODUCCIÓN El hormigón y los compuestos del cemento son materiales tolerantes y con una larga vida en servicio a temperatura ambiental extrema. Las temperaturas extremas en climas calientes y fríos no constituyen una amenaza, porque el...