SLAP 2010 Revista Iberoamericana de Polímeros Diciembre de 2010
Córdoba et al. Materiales reforzados
SLAP 2010 417 Rev. Iberoam. Polím., 11(7), 417-427 (2010)
APROVECHAMIENTO DE POLIPROPILENO Y POLIETILENO DE ALTA DENSIDAD RECICLADOS, REFORZADOS CON FIBRA VEGETAL, TETERA (Stromanthe Stromathoides)
Carlos Córdoba*, Jenny Mera, Diego Martínez, Jesús Rodríguez
Centro de investigaciones enmateriales, Ciudadela universitaria Torobajo, Universidad de Nariño, Pasto, Colombia. Correo electrónico: carcob@udenar.edu.co
RESUMEN
Este trabajo expone cómo la mezcla en proporciones adecuadas de PP (polipropileno y PEAD (polietileno de alta densidad) reciclados, como matriz polimérica, reforzada con cantidades óptimas de fibra natural tetera (Stromanthe stromathoides), permiten obtener materialesa mas bajos costos y que pueden reemplazar a los usados actualmente, especialmente productos de madera superando sus propiedades de ductilidad y de durabilidad, al mismo tiempo que, se contribuye significativamente a mitigar impactos ambientales negativos.
Se examinan las propiedades fisicoquímicas de la incorporación de fibra, para cada producto reciclado. La fibra tetera como materia prima fuemolida en molino de discos, hasta un tamaño de 1 a 3 mm que es el utilizado como refuerzo. El PP se recicló de tapas de botellas, seleccionadas y fracturadas manualmente con martillo y cortadas a tamaño variables entre 3 y 5 mm. El PEAD, se tomó de bolsas plásticas variables, que se despedazan manualmente y posteriormente se peletizan en la empresa Cooemprender de la ciudad de Pasto, en tamañoaproximado de 2-5 mm. Los análisis bromatológicos de la tetera y las pruebas mecánicas de los materiales compuestos, se efectuaron en los laboratorios de la Universidad de Nariño. Para las pruebas mecánicas se aplicaron las normas ASTM D1037, especiales para paneles aglomerados. Se encontró que las pruebas de flexión, compresión y tensión originan un aumento de la ductilidad, en detrimento de unabaja de su resistencia, lo cual hace de este material reforzado, un material adecuado para productos como la madera plástica.
Palabras claves: material compuesto, PP reciclado, PEAD reciclado, tetera, reciclaje
ABSTRACT
This work shows how the mixture in adequate proportions of PP (polypropylene and PEAD (high density polyethylene) recycled, used as a polymeric matrix and reinforced with optimalquantities of tetera natural fiber (Stromanthe stromathoides), lets to obtain the cheapest materials which can replace those used at present This mixture can overcome the wooden products related to its ductibility and durability characteristics, at the same time, it contributes to decrease the negative environmental impacts.
The physical and chemical characteristics of fiber incorporation aretested in every recycled product. The tetera fiber used as raw material was milled in dicks mills. It was obtained a 1 – 3 mm size which is adequately used as reinforce. The PP was obtained from bottles lids. They were selected and broken by hand with a hammer; cut in different sizes from 3 to 5 mm. The PEAD was taken from several plastic bags, which are destroyed by hand and later, they are pelletedin 2–5 mm size. This process was executed in the Cooemprender enterprise locates in the city of Pasto. The bromatological analysis of
SLAP 2010 Revista Iberoamericana de Polímeros Diciembre de 2010
Córdoba et al. Materiales reforzados
SLAP 2010 418 Rev. Iberoam. Polím., 11(7), 417-427 (2010)
tetera and the mechanical tests of compound materials were carried out in the University of Nariño’slaboratories. ASTM D137 regulations were used in mechanic tests, which are special to agglomerated panels. It was found that an increase of ductibility is resulted from flexion, compression and tension tests, to the detriment of its low resistance, so that this compound could be an adequate material in products as the plastic wooden.
Key words: compound material, PP recycled, PEAD recycled,...
Leer documento completo

Regístrate para leer el documento completo.

Estos documentos también te pueden resultar útiles

  • El polietileno
  • Polietileno
  • Polietileno
  • Polietileno
  • Polietileno
  • polietileno
  • Polietileno
  • POLIETILENO

Conviértase en miembro formal de Buenas Tareas

INSCRÍBETE - ES GRATIS