Caracterización mineralógica y química de los ladrillos
de la Torre del Oro de Sevilla: una aproximación a
la temperatura de cocción y origen de las materias primas
S. LEGUEY*, M.I. CARRETERO*, B. FABBRI**, E. GALÁN*
* Departamento de Cristalografía, Mineralogía y QuímicaAgrícola. Facultad de Química. Universidad de Sevilla. s/n. 41012 Sevilla
** Istituto di Richerche Tecnologiche per la Ceramica. C.N.R. 48018 Faenza. Italia

La Torre del Oro es un edificio almohade del siglo XIII de tres cuerpos, con fábrica de ladrillo en el segundo y tercer cuerpo.
De acuerdo con el análisis mineralógico se han diferenciado dos grupos de ladrillos. El primero se caracterizapor la presencia de illita y el desarrollo incipiente o nulo de fases de alta temperatura (gehlenita, wollastonita). Presentan coloraciones rojizas y pasta con textura microcristalina. Estos ladrillos se cocieron entre 800-850ºC. Para el segundo grupo la temperatura de
cocción se encuentra entre 850-900ºC, según se deduce de la ausencia de illita y de la presencia en cantidades importantes degehlenita y wollastonita-diopsido. La pasta es verde oscura e isótropa, presentando los ladrillos colores claros. El estudio de
la evolución de las fases en los ladrillos calentados en el laboratorio a 800 y 900ºC concuerda razonablemente con los márgenes de cocción deducidos del estudio mineralógico. La composición química de los ladrillos es muy homogénea y similar
a la de los materialesterciarios de la Formacion Écija (margas azules) y de ciertos niveles de la Serie de Transición, ambos
con afloramientos muy próximos a Sevilla, que pudieron ser empleados para la fabricación de estos ladrillos.
Palabras clave: Torre del Oro, ladrillos, temperatura de cocción, margas azules
Mineralogical and chemical characterization of the bricks from the Torre del Oro, Seville (Spain).
An approachto firing temperature and the origin of the raw materials
The Torre del Oro is a Moslem building of three bodies dating from the 13th Century. The second and third bodies are built
with bricks. According to mineralogical analysis two main groups of bricks can be established. A first group of bricks contents illite and low amounts of gehlenite and wollastonite. They are reddish and present amycrocristalline matrix. The firing
temperature ranges between 800-850ºC for this group. Firing temperatures for the second group ranged between 850-900ºC,
because of the absence of illite, and the presence of important amounts of gehlenite and wollastonite-diopside. They are yellowish and present a green coloured isotropic matrix. Mineralogical compositions of laboratory firing samples at 800ºCand
900ºC agree reasonably with the estimated firing temperature. Chemical composition presents no differences among the
samples, being quite similar to Tertiary sediments from the Ecija Formation (blue marls) and the Transition Series (silts).
These materials crop out quite near Seville, and have been traditionally used in the local tile industry.
Key words: Torre del Oro, bricks, firingtemperature, blue marls

1. INTRODUCCIÓN
En los últimos años han aumentado las investigaciones
dedicadas a ladrillos y morteros empleados en monumentos
del Patrimonio Español (1), (2), (3), (4). Estas investigaciones
están en línea con los estudios que desde hace años se siguen
en otros países europeos sobre estos materiales (5), (6), (7), (8).
Estos trabajos han incorporado la metodología ytécnicas propias de la caracterización de cerámicas arqueológicas, con un
doble objetivo: a) determinar el estado de conservación de los
materiales, conocer su origen y definir las diferentes tecnologías de fabricación (aspectos arqueométricos), b) profundizar
en el comportamiento de estos materiales frente a los agentes
de degradación, con la finalidad de adoptar medidas de protección y...