Recuperacion De La Plata

23 (2009) 9-16

RECICLAJE DE CHATARRA DE JOYERÍA PARA LA RECUPERACIÓN HIDROMETALÚRGICA DE PLATA
Carol Barrientos, Alfonso Martins Universidade Federal de Minas Gerais-UFMG Curso de Pós-Graduação em Engenharia Metalúrgica e de Minas-CPGEM Rua Espírito Santo 35 sala 206-AG, Centro, Belo Horizonte, Minas Gerais, Brasil cebarrientos@gmail.com RESUMEN Muchos residuos valiosos generados en lafabricación de joyería se pierden, por la falta de conocimiento técnico de la recuperación de los metales preciosos usados en su elaboración. Este trabajo presenta los resultados experimentales del uso de un método hidrometalúrgico para tratar chatarra de joyería de oro, utilizando muestras con proporciones mayores y menores de 10% de Ag. El método adoptado consistió de una lixiviación de las muestrascon HNO3, donde se empleó el método factorial completo a dos niveles experimentales para evaluar la influencia de: tiempo de lixiviación, temperatura de la solución acuosa de lixiviación y la relación sólido/líquido, sobre el porcentaje de extracción metálica. Posteriormente, fue utilizado el método de optimización estadística del paso ascendente para determinar las condiciones experimentalesóptimas para alcanzar el máximo porcentaje de extracción de la plata. Las condiciones óptimas para la total lixiviación de Ag con HNO3 para 0,5 g de muestra fueron: 32 mL de HNO3, 1.5 h y 42°C para la muestra 1 y 45 mL de HNO3, 2.25 h y 43°C para la muestra 2; y el mejor resultado para la recuperación de la plata (94% de Ag) se obtuvo por la calcinación del AgCl resultante de la adición de NaCl al licorde HNO3. Palabras claves: plata, chatarra de joyería, recuperación, lixiviación, hidrometalurgia. ABSTRACTA great amount of scrap metal wastes away in the manufacturing of jewelry, which due the lack of knowledge of precious metals recovery used in its manufacturing. This work presents the experimental results of the use of a hydrometallurgical method to treat gold jewelry scrap using sampleswith proportions higher and lower than 10% Ag. The adopted method consisted of samples, leaching with HNO3 to extract the silver, where was used the complete Factorial Method with two experimental levels to evaluate the influence of the variables on the experimental response: leaching time, aqueous leaching solution temperature and solid/liquid ratio, on the metallic extraction percentage. Theascending step method for statistical optimization was used after the factorial method aiming at determining the optimum experimental conditions to reach the maximum silver extraction percentage. The leaching liquors were treated and three methods were evaluated for the silver recovery. The optimum conditions for total Ag leaching with HNO3 were: 32 mL of HNO3, 1.5 h and 42°C for sample 1 and 45 mL ofHNO3, 2.25 h and 43°C for sample 2, and the best result obtained to the silver recovery (94% of Ag) occurred by the AgCl calcination obtained with the NaCl added to the HNO3 liquor. Keywords: silver, scrap jewelry treatment, recovery, leaching, hydrometallurgy. 9

C. Barrientos; A. Martins 23 (2009) 9-16

1. INTRODUCCIÓN El oro (Au), la plata (Ag) y otros metales preciosos son empleados en lafabricación de joyas aleados con otros metales. Estos metales preciosos son escasos en la naturaleza, a pesar de que su cantidad aumenta cada año como resultado de la minería, la proporción es menor en comparación con la demanda existente [1]. Esto ha provocado un alza en el precio promedio de estos metales preciosos. Además del alto costo de los metales preciosos, muchos residuos valiosos songenerados en la fabricación de joyería, los cuales se pierden por la falta de conocimiento de su recuperación [2]. Una gran parte de estos residuos contienen altas proporciones de metales preciosos, especialmente de oro. Estos residuos son fáciles de tratar, ya que están formados únicamente por metales, algunos deseables porque forman parte de la aleación inicial y otros que han sido incorporados...