Sirderurgia

METHODOLOGY FOR METALLOGRAPHIC STUDY OF DEFECTS IN CARBON STEEL LONG PRODUCTS
Luis Reda(1) Cristian Genzano(1) Jorge Madías(1)

ABSTRACT In this paper the methodology for the study of defects in carbon steel long products in use at IAS for Latin American steel plants is presented. This work is focused on the defects observed in low, medium and high carbon wire rod, bar, rebar, flats andshapes, originated in continuous casting or rolling. The study of defects has many aspects to be taken into account before metallographical analysis. The general information about the defect like frequency, size, shape and position, based on naked eye observation is very important. It is also a must the observation with magnifying glass of the surface, as rolled or descaled with mechanical or chemicalmethods (sand blasting, shoot peening or pickling). The study of the internal quality of continuous casting products based on transverse cuts can also give important information to determine the origin of the defects. The metallographical study of polished samples is used includes their observation in the light microscope in the aspolished state or with the help of various reagents. Depending ofthe steel grade and the problem being searched, Nital, Oberhoffer´s reagent, alkaline sodic chromate, Béchet Beaujard´s or other etchants can be selected. Each observation gives different insights on the process step where the defect started, its possible location in the parent as cast product, its evolution during preheating or rolling, etc. Extra information can be taken from the SEM and EDSanalysis (especially when the defect is associated with nonmetallic inclusions or fractures). Follow up of continuous casting and rolling process and in-plant tests are useful tools in order to verify hypotheses and to improve practices to avoid defects. Literature surveys usually give insight, as defects are usually repetitive from plant to plant. Key words: defects, long products, reagents,continuous casting, rolling.

(1) Instituto Argentino de Siderurgia, Av. Central y Calle 19 Oeste, 2900 San Nicolas, Prov. de Buenos Aires, Argentina, www.cablenet.com.ar/ias/eng/aceria.htm

13th IAS Steelmaking Seminar, 2001, Buenos Aires, Argentina

743

METODOLOGÍA PARA EL ESTUDIO METALOGRÁFICO DE DEFECTOS EN PRODUCTOS LARGOS DE ACERO AL CARBONO.
Luis Reda Cristian Genzano Jorge Madías

1.INTRODUCCION. En este trabajo se revisa la metodología utilizada en el Instituto Argentino de Siderurgia para estudiar causas de defectos en productos de aceros al carbono en plantas de América Latina, y los diferentes reactivos metalográficos que pueden ser utilizados para brindar mayor información acerca del origen de los mismos. Se centra en defectos observados en productos largos de aceros alcarbono, tales como alambrón de acero de bajo, medio y alto carbono, barras para construcción mecánica de bajo y medio carbono, barras para refuerzo de hormigón, planchuelas y perfiles. 2. METODOLOGIA PARA DETERMINACIÓN DEL ORIGEN DE DEFECTOS. La determinación del origen de defectos incluye la observación de aspectos generales, tales como la frecuencia de ocurrencia, preferencia por una arista ouna cara determinada en la palanquilla, posición en la barra o alambrón (una generatriz o varias, continuo o discontinuo), mayor frecuencia para ciertos grados de aceros, etc. También es importante el estudio detallado del aspecto visual que ofrece el defecto, con ayuda de la lupa estereoscópica, así como la observación de muestras pulidas, generalmente transversales, del producto laminado opalanquilla y finalmente su estudio microscópico a mayores aumentos bajo ataque con diversos reactivos. La información del desarrollo de los procesos de colada continua y de la laminación es necesaria y puede aportar siempre datos de importancia. También a veces es necesario diseñar seguimientos de coladas en la acería y en la laminación. En este trabajo la mayor atención va estar dada a los aspectos...