R. Contreras Bustos / J. R. Rosas Cedillo / A. J. Ruiz García
CARACTERIZACIÓN DE UN RESIDUO CON ALTO CONTENIDO DE ALUMINIO
Revista Mexicana de Ingeniería Química, año/vol. 2, número 003
Universidad Autónoma Metropolitana - IztapalapaDistrito Federal, México
pp. 109-116

Red de Revistas Científicas de América Latina y el Caribe, España y Portugal
Universidad Autónoma del Estado de México

REVISTA MEXICANA DE INGENIERÍA QUÍMICA Vol. 2 (2003) 109-116

AMIDIQ

CARACTERIZACION DE UN RESIDUO CON ALTO CONTENIDO DE ALUMINIO
CHARACTERIZATION OF A RESIDUE WITH HIGH ALUMINUM CONTENT
R. Contreras-Bustos 1 *, J. R.Rosas-Cedillo 2 y A. J. Ruiz-García 1
1

CIDETEQ S. C., Depto. Tecnología Ambiental. Parque Tecnológico Querétaro Sanfandila
76700 Pedro Escobedo, Querétaro.
2
Depto. I. P. H. Universidad Autónoma Metropolitana- Iztapalapa, San Rafael Atlixco No. 186, 09340 México, D.F.
Resumen
Un residuo proveniente del proceso de lavado químico del aluminio se sometió a caracterización con el objetivo deobtener datos que permitieran vislumbrar un proceso para su aprovechamiento. De los resultados de difracción de
rayos X se obtuvo que el residuo esta compuesto principalmente de gibbsita acompañada de boehmita lo cual se
aproximó a los resultados de los análisis químicos de donde se obtuvo que el residuo tiene 32.65 % de aluminio,
teniendo como impurezas principalmente sodio y magnesio conporcentajes de 0.38 y 0.17 %, respectivamente. Los
tamaños de los granos fueron de aproximadamente 10 µm en promedio. El análisis térmico diferencial mostró que el
residuo sufre transformaciones al ser calentado, obteniéndose γ-Al2O3 a 800 OC. Se determinó que el área superficial
es igual a 147.40 m2/g y el diámetro de poro es de 38 Å. Con los datos obtenidos se concluyó que el residuo tiene
potencialpara ser aprovechado de tres formas: para obtener alúmina abrasiva, para obtener sulfato de aluminio y
como alimentación al proceso de refinado de alúmina.
Palabras clave: caracterización, residuo, alúmina, gibbsita.
Abstract
A residue from the chemical washing process of aluminum was characterized by different techniques in order to
envisage different re-utilization schemes. The residue wascomposed mainly by gibbsite and boehmite in lower
amounts. The chemical analyses reported 32.65 % aluminum and sodium and magnesium as impurities (0.38 and
0.17 % respectively). The powder grain size was around 10 µm. Changes in the structure of the residue were found
by Differential Thermal Analysis. After heating the residue to 800 OC, γ-Al2O3 was identified. The surface area was
147.40 m2/gand the pore diameter was 38 Å. From the characterization data we propose that the residue can be reutilized in three ways: as an abrasive, in production of aluminum sulfate or in the alumina refining process.
Keywords: characterization, residue, alumina, gibbsite.

1. Introducción
El aluminio es uno de los elementos
más abundantes en la corteza terrestre
(Pehlke, 1973; Hayes, 1985;Kirk-Othmer,
1967), encontrandose normalmente en forma
de silicato de aluminio puro o mezclado con
otros metales y como óxidos, pero nunca
como metal libre. Los silicatos no son menas
útiles porque es extremamente difícil y por
tanto muy caro, extraer el aluminio de ellas.
En la producción de aluminio la principal
materia prima es la bauxita, que llega a
contener al menos 40% de óxido dealuminio. En el mundo existen numeroso

depósitos de bauxita principalmente en las
zonas tropicales y subtropicales del mundo.
Usualmente se requieren de 4 a 6 toneladas de
bauxita para producir una tonelada de
aluminio, lo que provoca una gran
deforestación durante su extracción.
La alúmina dependiendo de su pureza, puede
emplearse para varios fines tales como:
sensores de humedad (Goto,...