Tablas Aisi De Aceros

Aceros al Carbono | Descripción |
1OXX | no-resulfurado, 1.00 Mn máx |
IlXX | resulfurado |
12XX | resulfurado y refosforizado |
15XX |no-resulfurado, sobre 1.00 Mn máx |
Aceros aleados | |
13XX | 1.75 Mn |
40XX | 0.20 o 0.25 Mo, o 0.25 Mo + 0.042 S |
41XX | 0.50, 0.80 o 0.95 Cr + 0.12, 0.20 o0.30 Mo |
43XX | 1.83 Ni, 0.50-0.80 Cr, 0.25 Mo |
46XX | 0.85 o 1.83 Ni + 0.20 o 0.25 Mo |
47XX | 1.05 Ni, 0.45 Cr, 0.20 o 0.35 Mo |
48XX | 3.50 Ni +0.25 Mo |
51XX | 0.80, 0.88, 0.93, 0.95 o 1.00 Cr |
51XXX | 1.03 Cr |
52XXX | 1.45 Cr |
61XX | 0.60 o 0.95 Cr + 0.13 o 0.15 V min |
86XX | 0.55 Ni,0.50 Cr, 0.20 Mo |
87XX | 0.55 Ni, 0.50 Cr, 0.25 Mo |
88XX | 0.55 Ni, 0.50 Cr, 0.35 Mo |
92XX | 2.00 Si o 1.40 Si + 0.70 Cr |
50BXX | 0.28 o 0.50 Cr,0.0005 - 0.003 B |
51BXX | 0.80 Cr, 0.0005-0.003 B |
81BXX | 0.30 Ni, 0.45 Cr, 0.12 Mo, 0.0005 - 0.003 B |
94BXX | 0.45 Ni, 0.40 Cr, 0.12 Mo, 0.0005 -0.003 B |

Sufljo AISl | Sufijo UNS | Descripción |
xxxL | xxxO1 | bajo carbono < 0.03% evita SCC |
xxxS | xxx08 | bajo carbono < 0.08% |
xxxN| xxx51 | nitrógeno agregado mayor resistencia |
xxxLN | xxx53 | bajo C < 0.03% + N agregado |
xxxF | xxx20 | mayor S y P mejor mecanizado |
xxxSe| xxx23 | Selenio mejor mecanizado |
xxxB | xxx15 | Si agregado evita descamado |
xxxH | xxx09 | Mayor contenido de carbono |
xxxCu | xxx30 | Cobreagregado |
Tablas obtenida de Nomenclatura de aceros. Tubocobre.net. obtenida de http://www.tubocobre.net/literatura_pdf/cobre_nomenclatura_acero.pdf