LA SOLUBILIDAD DIFERENCIAL DE LA POLIAMIDA 6

INTERPRETACIÓN DE LA SOLUBILIDAD DIFERENCIAL DE LA POLIAMIDA 6

J. Gacén *, D. Cayuela**, M. Tzvetkova*** y M.A. Mójica****

0. 1.

compositions was determined by viscosimetry and
their crystallinity was determined by DSC. The
molecular weight of the dissolved fraction in each
test was also determined.This allowed the changes
in differential solubility of the polyamide 6 fibres
according to temperature to be interpreted.
The results obtained show that the
molecular weight of the undissolved and dissolved
fractions in the differential solubility test increases
with the percentage of material dissolved, as a
result of the increased phenol content of the
Ph/2POH
mixture.
The
enthalpy
offusion/crystallinity also increases with the molecular
weight of the insoluble fraction.

Resumen

De las fracciones no disueltas resultantes
del ensayo de solubilidad diferencial de un hilo
continúo
de
poliamida
6
en
mezclas
fenol/isopropanol
(Ph/2POH)
de
diferente
composición, se han determinado el peso
molecular por viscosimetría y su cristalinidad por
DSC. También se ha determinado indirectamente elpeso molecular de la fracción disuelta en cada
ensayo. Ello ha permitido interpretar la evolución de
la solubilidad diferencial de las fibras de poliamida
6 en función de la temperatura del ensayo.
Los resultados obtenidos indican que el
peso molecular de las fracciones no disueltas y
disueltas en el ensayo de solubilidad diferencial
aumenta a medida que aumenta el porcentaje de
material disuelto,como consecuencia del aumento
del contenido de fenol en la mezcla Ph/2POH.
También aumenta la entalpía de fusión/cristalinidad
al aumentar el peso molecular de la fracción no
soluble.
Palabras clave: poliamida 6, solubilidad diferencial,
residual, peso molecular, cristalinidad

0.2.

Key words: polyamide 6, differential solubility, residual fraction,
molecular weight, crystallinity

0.3.

fracciónSummary: INTERPRETATION OF
THE DIFFERENTIAL SOLUBILITY
OF POLYAMIDE 6 ACCORDING
TO TEMPERATURE

The molecular weight of the undissolved
fractions resulting from the differential solubility test
of a filament yarn of polyamide 6 in
phenol/isopropanol mixtures (Ph/2POH) of different

*
**

***
****

Dr. Ing. Joaquín Gacén
Universidad jubilado.

Guillén.

Catedrático

de

Dra. en Ciencias Químicas,Diana Cayuela Marín.
Investigadora de la Universidad Politécnica de Cataluña.
Jefa del Laboratorio de Polímeros Textiles del INTEXTER
(U.P.C.).

Résumé: INTERPRÉTATION DE
LA SOLUBILITÉ DIFFÉRENTIELLE
DU POLYAMIDE 6 EN FONCTION
DE LA TEMPÉRATURE

À partir de fractions non dissoutes, issues
de l’essai de solubilité différentielle d’un fil continu
de
polyamide
6
dans
des
mélanges
phénol/isopropanol(Ph/2POH) de différente
composition, l’étude a déterminé le poids
moléculaire par viscosimétrie et la cristallinité par
DSC. Le poids moléculaire de la fraction dissoute
dans chaque essai a également été déterminé.
Cela a permis d’interpréter la solubilité différentielle
des fibres de polyamide 6 en fonction de la
température de l’essai.
Les résultats obtenus indiquent que le poids
moléculaire desfractions non dissoutes et des
fractions dissoutes dans l’essai de solubilité
différentielle augmente à mesure que le
pourcentage de matière dissoute augmente, suite à
l’augmentation du contenu de phénol dans le
mélange Ph/2POH. L’entalpie de fusion/cristallinité
augmente aussi avec l’augmentation du poids
moléculaire de la fraction non soluble.
Mots clés: polyamide 6, solubilité différentielle,fraction
résiduelle, poids moléculaire, cristallinité

M. Tzvetkova. Ing. Industrial
M.A. Mójica. Ing. Industrial

BOLETíN INTEXTER (U.P.C.) 2005. Nº. 127

31

J. Gacén, D. Cayuela, M. Tzvetkova y M.A. Mójica
LA SOLUBILIDAD DIFERENCIAL DE LA POLIAMIDA 6

1.

INTRODUCCIÓN

La solubilidad diferencial de una fibra se
define como el porcentaje de ella disuelto en una
determinada mezcla disolvente/no...