anodizado acero

Artículo Regular
www.rlmm.org

ANODIZACIÓN DE ACEROS INOXIDABLES COMO TRATAMIENTO SUPERFICIAL PARA
LA OBTENCIÓN DE ESTRUCTURAS POROSAS
Pier Scheffel1, Luciane Fuhr2, José Matos2, Sandra Kunst2, Gustavo Ludwig2, Célia Malfatti2,
Claudia Oliveira1*
1: Universidade Feevale, Instituto de Ciencias Exactas y Tecnológicas, Programa de Posgrado en Tecnología de
Materiales y Procesos Industriales,Carretera RS 239, Nº 2755, Novo Hamburgo, Brasil. 2: Universidade Federal do Rio
Grande do Sul, Escuela de Ingeniería, Departamento de Ingeniería Metalúrgica, Av. Bento Gonçalves 9500, Sector 4,
Prédio 75, Porto Alegre. Brasil.
*e-mail: cto@feevale.br

RESUMEN
El objetivo del presente trabajo es obtener una estructura porosa en acero inoxidable ferrítico (AISI-430) mediante el
proceso deanodizado, debido a la gran demanda como metales decorativos. El método de anodización tiene gran utilidad
en procesos decorativos porque forma un óxido del tipo poroso de diversos colores. En este contexto se busca anodizar el
acero inoxidable ferrítico en un electrolito comercial INCO (CrO3 [2,5 M] + H2SO4 [2,5 M]) por medio de la aplicación de
una corriente continua, variando el tiempo deanodizado a fin de obtener una estructura porosa. Los sistemas se
caracterizaron con respecto al comportamiento electroquímico mediante las curvas de polarización y la monitorización del
potencial de circuito abierto (OCP). El comportamiento morfológico se evalúa por microscopía electrónica de barrido
(MEB) y microscopía de fuerza atómica (AFM). Los resultados muestran que el tiempo de anodizadono influye en el
comportamiento electroquímico de todos los sistemas y que éstos forman una estructura porosa. Además, se demuestra que
el proceso de disolución es más intenso que la formación de óxidos.
Palabras Claves: Anodización, acero ferrítico, estructura porosa, MEB, AFM

STAINLESS STEELS AS ANODIZING SURFACE TREATMENT FOR OBTAINING POROUS
STRUCTURES
ABSTRACT
The aim of this work isto obtain a porous structure in ferritic stainless steel (AISI-430) by anodization process. The
anodization method is highly useful in processes for forming a decorative porous oxide film of various colors. In this
context, ferritic stainless steels was anodized in a commercial electrolyte INCO (CrO3 [2,5 M] + H2SO4 [2,5 M]), appling a
continuous current, varyng the anodization time, to get aporous structure. Systems are characterized by the
electrochemical behavior means polarization curves and monitoring the open circuit potential (OCP). Morphological
behavior was assessed by scanning electron microscopy (SEM) and atomic force microscopy (AFM). Results show that
the anodizing time does not affect the electrochemical behavior in all systems and that these form a porous structure,moreover verified that the dissolving process is more intense than the formation of oxides.
Keywords: Anodizing, ferritic stainless steel, porous structure, SEM, AFM

Recibido: 29-10-2012 ; Revisado: 11-05-2013
Aceptado: 29-05-2013 ; Publicado: 26-07-2013

189

pISSN: 0255-6952 | eISSN: 2244-7113
Rev. LatinAm. Metal. Mat. 2014; 34 (2): pp-pp

Artículo Regular
www.rlmm.orgperforación hacia un extremo. Estas probetas fueron
desbastadas con papeles de carburo de silicio (Nº
100, 220, 400, 600, 800, 1200, 2400 y 4000) y
pulidas con pasta de diamante de 1 µm. La
anodización se realizó en un electrolito
convencional INCO (H2SO4 + HCrO4 [2,5 M]),
aplicando una densidad de corriente de 400 mA/cm2
y diferentes tiempos (10, 30 y 60 min) utilizando
como ánodo el aceroinoxidable ferrítico y como
cátodo el electrodo de platino.

1. INTRODUCCIÓN
Los aceros inoxidables ferríticos, en especial el
acero AISI-430 poseen excelentes características,
como, conductividad eléctrica, resistencia mecánica
y resistencia a la corrosión, por lo que son utilizados
ampliamente en diversas aplicaciones industriales y
decorativas [1, 2]. Estudios recientes han despertado
el...