Reactividad árido-álcali en áridos empleados para hormigón
The alkali–aggregate reaction for various aggregates used in concrete
J. Gadea(*), J. Soriano(**), A. Martín(*), P. L. Campos(*), A. Rodríguez(*), C. Junco(*),
I. Adán(*), V. Calderón(*)
Recepción/Received: 22-VII-2008Aceptación/Accepted: 27-III-2009 Publicado online/Online publishing: 11-VIII-201
RESUMEN
Este trabajo pretende contribuir al conocimiento de las reacciones de interacción entre los áridos y los componentes
de la fase intersticial del hormigón y determinar si estos áridos, empleados posteriormente en la fabricación del hormigón, son reactivos y por tanto susceptibles de provocar una disminución progresiva desus propiedades iniciales.
Para la caracterización de cada árido se ha realizado un estudio petrográfico, fundamental a la hora de determinar
su posterior comportamiento en términos de reactividad
frente a diversos factores. Seguidamente, se ha analizado la reactividad potencial de diferentes áridos silicatados (pizarras, gneis, corneanas, granitos, cuarcita y serpentina) mediante los dosmétodos normalizados existentes: el método químico para la determinación de la reactividad potencial de áridos y el método acelerado en probetas de mortero; y para contrastar ambos hemos seguido el método de la reactividad superficial.
Los resultados determinan que algunos áridos son susceptibles
de reaccionar con los componentes de la fase intersticial
de hormigón. La observación de su textura antesy después
del ataque denota la existencia de esta interacción.
Palabras clave: reacción álcali-sílice, degradación, expansión, mortero, SEM.
SUMMARY
The aim of this work is to contribute to the knowledge of the interactions between aggregates and the components of the interstitial phase of concrete and to determine whether those aggregates that are subsequently used in the manufacture ofconcrete are reagents and are therefore likely to undergo a progressive deterioration of their initial properties.
An initial petrographic study of each aggregate is performed in order to be able to determine its subsequent behaviour and reactivity under the influence of various factors. The potential reactivity of different silicaceous aggregates (slates, gneiss, hornfels, granites, quartzite andserpentine) is then determined by a chemical method for evaluating the potential reactivity of aggregates and an accelerated method in mortar specimens, and finally the surface reactivity is investigated.
The results of these studies suggest that some aggregates are able to react with the components of the interstitial phase of concrete. The existence of this kind of interaction is confirmed by theresults of the surface investigations before and after the basic reaction.
Keywords: alkali–silica reaction, degradation, expansion, mortar, SEM.
(*) Universidad de Burgos (Burgos, España).
(**) Laboratorio Central de Estructuras y Materiales (CEDEX-Ministerio de Fomento) (Madrid, España). Persona de contacto/Corresponding author: vcalderon@ubu.es
J. Gadea et al.
1. INTRODUCCIÓN
Una reacciónálcali-silicato se produce cuando interaccionan
áridos, que contienen minerales silicatados potencialmente
reactivos, con los álcalis del cemento. Esta reactividad lleva consigo la formación de geles que en presencia de humedad se expanden, manifestándose en agrietamientos y movimientos diferenciales y con ello, una disminución drástica de la durabilidad (1-5) Por tanto,
este proceso vienedeterminado en gran medida con la humedad relativa del ambiente y la tensión mecánica a la cual esta sometida cada elemento estructural (6-11).
Las fases de la reacción árido-álcali se pueden dividir en dos: el primer paso de neutralización de los radicales Si-OH a través de una reacción tipo ácido-base, donde las cargas terminales son equilibradas por iones Na+, teniendo en cuenta que la...