zinalco

ÍNDICE
CAPITULO I. “ANTEPROYECTO” ABSTRACT……………………………………………………………………... 2
INTRODUCCIÓN………………………………………………………………. 4
JUSTIFICACIÓN……………………………………………………………….. 5
PLANTEAMIENTO DEL PROBLEMA……………………………………….. 6
OBJETIVOS…………………………………………………………………….. 7
HIPOTESIS……………………………………………………………………... 8
CAPITULO II. “MARCO TEÓRICO” PRIMER LÍNEA DE INVESTIGACIÓN………………………………………. 9
SEGUNDA LÍNEA DEINVESTIGACIÓN……………………………………. 10
TERCERA LÍNEA DE INVESTIGACIÓN……………………………………. 12
ANEXOS ANEXO 1………………………………………………………………………... 14
ANEXO 2………………………………………………………………………... 15
ANEXO 3………………………………………………………………………... 16
ANEXO 4………………………………………………………………………... 17
BIBLIOGRAFÍA…………………………………………………………………. 22
ABSTRACT

En México el zinc ha estado durante mucho tiempo subutilizado; con la idea de mejorar susaplicaciones, la investigación del material se inició para tratar de introducirlo en otros campos. Por otra parte, México no posee bauxita, mineral del que se extrae el aluminio, ante la escasa producción es necesaria la importación.
En nuestro país hay grandes yacimientos de zinc por lo que se ha trabajado en el desarrollo de aleaciones con el objeto de ampliar el campo de aplicación para este metal, delcual México es un importante productor a nivel mundial, y así evitar su desplazamiento por los plásticos y el aluminio. Los resultados de las investigaciones realizadas con este material condujeron al desarrollo de la aleación Zinalco la cual, puede tener diversas aplicaciones dada su posibilidad de ser transformada tanto por procesos de fundición y/o de deformación plástica.
El Zinalco es unaaleación desarrollada en el Instituto de Investigaciones en Materiales (IIM-UNAM), basada en Zn, que combina la alta resistencia mecánica de un acero estructural con la buena resistencia a la corrosión que presenta el aluminio y con un peso específico intermedio entre ambos. Esta combinación de propiedades aunado al bajo precio de la aleación, lo hacen apto para competir en el campo de aplicacionesdel aluminio.
ABSTRACT
In Mexico the zinc has been for a long time underutilized; with the idea of improving their applications, research of the material began to try to put it in other fields. On the other hand, Mexico has no bauxite, the ore from which aluminum is extracted, import is required before the scarce production.
In our country there are large deposits of zinc by what we haveworked on the development of alloys in order to extend the field of application for this metal, of which Mexico is a major producer worldwide, and prevent their displacement by plastics and aluminum. The results of investigations conducted with this material led to the development of Zinalco alloy which may have various applications due to its ability to be transformed both by casting and/or plasticdeformation processes.
The Zinalco is an alloy developed at the Institute for Research in Materials (IRM-UNAM), based on Zn, which combines the high mechanical strength of a structural steel with good resistance to corrosion that presents the aluminum and a specific weight intermediate between the two. This combination of properties in addition to the low price of alloy, make it fit to competein the field of applications of aluminum.
INTRODUCCIÓN
Como ya es sabido México no posee bauxita, siendo así, el aluminio que se utiliza suele ser importado.
Es por ello que se debe recurrir a diversas opciones que permitan dar una solución eficaz y eficiente, por lo cual una de las opciones que se ofrece es la utilización de la aleación de Zinc, Aluminio y Cobre; Se le llama ZINALCO por que esun palabra compuesta por las primeras letras de los metales que componen esta aleación:
ZINc, ALuminio y Cobre, donde el 80% pertenece al zinc, el 18% al aluminio y el 2% al cobre, los cuales se unen para crear uno nuevo con mejores y nuevas características a las de sus componentes originarios.
El Zinalco fue desarrollado por la Universidad Autónoma de San Luis Potosí y el Instituto de...