Efecto Del Mineral Trióxido Agregado, Cemento Portland E Hidróxido De Calcio En El Proceso De Reparación De Perforaciones Radiculares En Dientes De Canis Familiaris

Artículo Original

Alfonso Eugenio Bedoya Soria1 Carmen Rosa García Rupaya2
1 2

Efecto del mineral trióxido agregado, cemento portland e hidróxido de calcio en el proceso de reparación de perforaciones radiculares en dientes de Canis familiaris
Bedoya-Soria AE, García-Rupaya CR. Efecto del mineral trióxido agregado, cemento portland e hidróxido de calcio en el proceso de reparación deperforaciones radiculares en dientes de Canis familiaris. Rev Estomatol Herediana. 2009; 19(2):103-110. RESUMEN El propósito del estudio fue evaluar el efecto del Mineral Trióxido Agregado (MTA), el Cemento Portland (CP) y el Hidróxido de Calcio (Ca(OH)2) en el proceso de reparación de perforaciones radiculares en dientes de perros. Se utilizaron 4 perros mestizos de 1 año de edad. Mediante sedaciónendovenosa, se efectuaron tratamientos de conductos a 60 dientes para realizar perforaciones radiculares intencionadas e inmediatamente tratarlos con cada uno de los cementos a evaluar. Las muestras se obtuvieron a los 15 y 60 días, sacrificando a los animales, mediante una inyección letal. El proceso de reparación fue evaluado con un análisis histológico de las muestras, aplicándosele el test deKruskal-Wallis, y el test U de Mann-Whitney. 15 días después del tratamiento, se obtuvieron 6 casos con proceso de reparación al usar MTA, 2 casos al usar CP y ninguno al usar Ca(OH)2, encontrándose diferencias significativas, (P0,05), el resto mostró tejido conectivo con infiltrado inflamatorio, presencia de polimorfonucleares, linfocitos e histiocitos y algunas células plasmáticas. Comoconclusión el MTA indujo una mejor respuesta en el proceso de reparación de las perforaciones radiculares que el CP y el Ca(OH)2 a los 15 días y una similar respuesta que el CP a los 60 días. Palabras clave: MINERAL TRIÓXIDO AGREGADO / CEMENTO PORTLAND / HIDRÓXIDO DE CALCIO. Effect of MTA, portland cement and calcium hydroxide in the process of repair of root perforations in Canis familiaris teeth ABSTRACTThe purpose of the research was to assess the effect of Mineral Trioxide Aggregate (MTA), Portland Cement (PC) and calcium hydroxide in the repair process of root perforation in canine teeth. Four one-year-old mongrels were used and by venous sedation root canal theraphy were performed in sixty teeth. Later, deliberate root perforations were made and treated with each of the cements studies. Thesamples were obtained after fifteen and sixty days respectively using a lethal shot the animals were sacrificed. The repair process was evaluated with a histological analysis of the samples applying Kruskal-Wallis and Mann-Whitney U tests. Fifteen days after the treatment, six cases of repair process were obtained using MTA, two cases using Portland Cement and none using calcium hydroxide. As aresult, statistical significant differences (P0.05) were found in these samples while the rest of the cases showed connective tissue with inflammatory infiltrate along with polymorphonuclei, lymphocytes and hystocytes and some plasma cells. In conclusion MTA induced a better result in the repair process of the root perforations than Portland Cement and Calcium Hydroxide after fifteen days and similarresult as Portland Cement after sixty days. Key words: MINERAL TRIOXIDE AGGREGATE / PORTLAND CEMENT / CALCIUM HYDROXIDE.

Cirujano-Dentista, Magíster en Estomatología Docente del Departamento Académico de Medicina, Cirugía y Patología Oral. Facultad de Estomatología. Universidad Peruana Cayetano Heredia.

Correspondencia
Alfonso Eugenio Bedoya Soria Pasaje Adán Mejía 103 - 204 - Lima 14,Perú Teléfono: 4710166 / 999001421 e-mail: alfonsobedoya@hotmail.com

Recibido : 23 de junio del 2009 Aceptado : 30 de agosto del 2009

Introducción Las perforaciones radiculares laterales son accidentes que pueden ocurrir durante la apertura cameral, en un tratamiento de conductos ó durante la ampliación de la cámara pulpar cuando se desea colocar pernos. En algunos casos es tan grande o...