Practiica 2
BITACORA DEL ENSAYO
ACERO SUAVE A 618
LONGITUD INICIAL
8
Area inicial
0.78697159
DIAMETRO INICIAL
1.001
LONGITUD FINAL
10.5
DIAMETRO FINAL
0.613
Area final
0.29512897
Longitud recta
8
No
CARGA
DESPLAZAMIENTO
DEFORMACION
ESFUERZO
puntos
(Lb)
DEL PISTON
UNITARIA
LB/in2
P
(in)
in/in
0
0
0
0
0
1
3410
0.001
426.25
4333.06623
2
6450
0.002
806.25
8195.97571
3
9160
0.003
1145
11639.5562
4
12370
0.004
1546.25
15718.4837
5
14830
0.005
1853.75
18844.3907
6
180200.006
2252.5
22897.9042
7
20780
0.007
2597.5
26405.0194
8
23640
0.008
2955
30039.204
9
26370
0.009
3296.25
33508.1984
10
29250
0.010
3656.25
37167.7968
11
31600
0.011
3950
40153.927512
31710
0.0115
3963.75
40293.7038
13
31520
0.012
3940
40052.272
14
31390
0.015
3923.75
39887.0818
15
31100
0.020
3887.5
39518.5806
16
31630
0.025
3953.75
40192.0483
17
31650
0.03753956.25
40217.4622
18
31700
0.050
3962.5
40280.9969
19
31800
0.10
3975
40408.0663
20
37200
0.20
4650
47269.8134
21
41400
0.30
5175
52606.7278
22
47200
0.50
5900
59976.7525
23
50200
0.706275
63788.8342
24
52200
0.90
6525
66330.222
25
53100
1.10
6637.5
67473.8466
26
53400
1.30
6675
67855.0547
27
53500
1.50
6687.5
67982.1241
28
53300
1.70
6662.5
67727.9853
29
530001.90
6625
67346.7772
30
52000
2.10000
6500
66076.0833
31
38800
2.5
4850
49302.9237
º En que consiste el ensayo estático de tensión
Consiste ensometer a una probeta normalizada a un esfuerzo axial de tracción creciente hasta que se produce la rotura de la probeta. Este ensayo mide la resistencia de un material a una fuerza estática o aplicadalentamente
º Mencionar y definir los puntos principales de la gráfica esfuerzo deformación unitario
Módulo de elasticidad o Módulo de Young, que cuantifica la proporcionalidad anterior. Es el...
Regístrate para leer el documento completo.