Termi

Influencia del tratamiento térmico de envejecimiento
en las propiedades mecánicas de los aluminios
6061 T6 y 6063 T5
Influence of aging heat treatment on the mechanical properties of aluminum
6061 T6 and 6063 T5
Carlos Arturo Bohórquez A.1*, Mauricio Sierra Cetina2, Javier Lemus3
Ingeniería Mecánica, Universidad libre, Bogotá, Colombia. *carlosa.bohorqueza@unilibrebog.edu.co
Departamentode Ingeniería Mecánica y Mecatrónica, Universidad Nacional de Colombia, sede Bogotá.
3
Departamento de Mecánica Universidad Libre, Bogotá - Colombia.

1
2

Fecha de recepción del artículo: 12/12/2010: Fecha de aceptación del artículo: 25/01/2011

Resumen

Palabras clave

Por su bajo peso y sus buenas propiedades mecánicas,
tradicionalmente las aleaciones de aluminio se
han empleadoen la fabricación de componentes
estructurales de aviones y partes de automotores.
Las aleaciones de Aluminio con magnesio-silicio (AlMg-Si), de la serie 6XXX, presentan una respuesta
aceptable al tratamiento térmico de envejecimiento;
la razón de ello es que los contenidos de magnesio y
silicio permiten el endurecimiento por precipitación,
fenómeno que cambia significativamente laspropiedades mecánicas de dicha aleación.

Envejecimiento, aluminio, 6061, 6063

Para este estudio se seleccionaron dos aluminios:
el 6061 T6 y el 6063 T5, los cuales se trataron
térmicamente a 120°C, 150°C y 180°C durante
8, 12, 24, 48 y 72 horas con un posterior temple
en agua. Se realizó un diseño experimental para
establecer el número de probetas necesarias que
permitieran analizar elfenómeno; posteriormente,
se desarrollaron pruebas de tensión
y de
forma que se pudiese verificar el cambio de
propiedades sufrido durante
el tratamiento
térmico. Los resultados se presentan en gráficas
de comportamiento que muestran la influencia
del tiempo y la temperatura en las propiedades
mecánicas de los aluminios seleccionados.
20

AVANCES Investigación en Ingeniería 13 (2010)Abstract
Due to low weight and good mechanical
properties, traditionally aluminum alloys
have been used in the manufacture of aircraft
structural components and automotive parts.
The Aluminum alloy with magnesium-silicon
(Al-Mg-Si), series 6XXX, show an acceptable
response to heat treatment aging, the reason is
that the contents of magnesium and allow silicon
precipitation hardening, aphenomenon that
significantly change the mechanical properties
of the alloy.
For this study we selected two Aluminum: 6061 T6
and 6063 T5, which were treated thermally at 120
° C, 150 ° C and 180 ° C for 8, 12, 24, 48 and 72
hours with subsequent quenching. An experimental
design was used to establish the number of
specimens necessary machinery to analyze the
phenomena was subsequently Stresstests and
developed so that it could verify suffered property
changes during heat treatment. The results are

presented in graphs showing behavior influence of
time and temperature on the mechanical properties
selected aluminums

Keywords
Againg, aluminium, 6061T6, 6063 T5.

Introducción
Los tratamientos térmicos de los aluminios
son de bastante importancia para modificarsustancialmente sus propiedades, un fenómeno que
afecta las aleaciones de aluminio aún a temperatura
ambiente, es conocido como envejecimiento
natural, si se realiza a una temperatura mayor ocurre
un tratamiento térmico de precipitación conocido
como envejecimiento artificial. El envejecimiento
puede afectar las aleaciones de la serie 6XXX,
2XXX y 7XXX.
La demanda de componentes más ligeros en laindustria especialmente la aeronáutica ha impulsado
en los últimos años el uso de aleaciones de aluminio.
El aluminio 6061 T6 y 6063 T5 que se seleccionan
para estas aplicaciones, presentan una buena
resistencia a la corrosión, excelente maleabilidad,
soldabilidad y buenas propiedades mecánicas que
brindan gran flexibilidad en el diseño y fabricación
de piezas [1].
Los tratamientos de...