Evaluación in vitro de filtración hacia conducto radicular
de dos sistemas de reconstrucción post endodóncica
In vitro assessment of root canal leakage of two
post-endodontic reconstruction systems
Dov Erik Merlín Martínez,* Ricardo Williams Vergara,§Federico Barceló SantanaII
RESUMEN

ABSTRACT

El objetivo de este estudio fue el de evaluar el grado de microfiltración en dos sistemas de reconstrucción postendodóncica, valorando la penetración de un colorante a lo largo de las restauraciones
realizadas con endopostes y cementos duales de resina. En este
estudio se emplearon 30 dientes premolares unirradiculares extraídos a los que se les realizótratamiento de conductos y almacenándolos en agua bidestilada a 37 oC. Se distribuyeron los dientes
en tres grupos de forma aleatoria, con diez dientes por cada grupo. La cementación de los postes se realizó en dos de los grupos,
usando los sistemas RelyX Fiber post (3M ESPE dental products)
y Parapost (Coltene-Whaledent). Las muestras fueron sometidas al
proceso de termociclado y posterior inmersiónen azul de metileno
por siete días a 36 oC. Posteriormente se diafanizaron las muestras
y fueron analizadas bajo microscopio, obteniendo los valores de penetración en milímetros. Los resultados mostraron que los dientes
tratados con el sistema Parapost presentaron menor microfiltración.
El grupo control mostró el mayor índice de microfiltración. El análisis estadístico con la prueba de Donettmostró diferencia estadísticamente significativa entre los sistemas Parapost y RelyX. Conclusión: Se demostró que el sistema de reconstrucción Parapost
(Coltene-Whaledent), el cual tiene una técnica de grabado ácido,
reportó menores valores de microfiltración, siendo los resultados
estadísticamente significativos con respecto a los obtenidos con el
sistema de reconstrucción RelyX (3M ESPE dentalproducts).

The aim of the present study was to assess the degree of
microleakage observed when using two different post-endodontic
reconstruction systems; this was achieved assessing penetration
of a dye along restorations performed with endodontic posts and
dual-cure resin cements. For the present study, 30 extracted, single
rooted premolars were used. Root canal treatment was performed on
the teethwhich were later stored in bi-distilled water at 37 oC. Teeth
were randomly allotted to three groups, all groups were comprised of
10 teeth. In two groups, post cementation was performed using the
systems RelyX Fiber Post (3M ESPE dental products) and Parapost
(Coltene-Whaledent). Samples were subjected to thermo-cycling
and later immersed in methylene blue for seven days at 36 oC. After
this,samples were subjected to a diaphanization process and were
then analyzed under a microscope; penetration in millimeters was
thus obtained. Results revealed that teeth treated with Parapost
system exhibited lesser microleakage. Control group experienced
the greater amounts of microleakage. Statistical analysis conducted
with Donett test showed statistically significant difference between
Parapost andRelyX systems. Conclusion: Parapost reconstruction
system (Coltene-Whaledent) with acid-etch technique exhibited
lower microleakage values. Results were statistically significant
when compared to those obtained with the RelyX reconstruction
system (3M ESPE dental products).

Palabras clave: Endoposte, termociclado, microfiltración.
Key words: Endodontic post, microleakage, thermocycling.INTRODUCCIÓN

influyentes en el pronóstico del tratamiento endodóncico.2,3

www.medigraphic.org.mx

Los dientes que han sido tratados endodóncicamente requieren ser reconstruidos. Dentro de los
tratamientos de reconstrucción se encuentran la colocación de endopostes, que son aditamentos que
permiten recuperar el tejido dentario perdido durante
la terapia endodóncica y facilitar la reconstrucción del...