Product Information Nov 2010
Ultramid® B3K
Polyamide 6
Product Description Ultramid B3K is an easy flowing, stabilized PA6 product for fast processing. Applications Typical applicationsinclude technical parts with wall thicknesses greater than 2 mm. PHYSICAL Density, g/cm³ Moisture, % (50% RH) (Saturation) RHEOLOGICAL Melt Volume Rate (275 °C/5 Kg), cc/10min. MECHANICAL Tensile Modulus,MPa 23°C Tensile stress at yield, MPa 23°C Tensile stress at break, MPa 23°C Tensile strain at yield, % 23°C Nominal strain at break, % 23°C Flexural Modulus, MPa 23°C IMPACT Izod Notched Impact, kJ/m²23°C Charpy Notched, kJ/m² 23°C -30°C Charpy Unnotched, kJ/m² 23°C -30°C THERMAL Melting Point, °C HDT A, ° C Coef. of Linear Thermal Expansion, Parallel, mm/mm °C ELECTRICAL Comparative TrackingIndex ISO Test Method 1183 62 Property Value 1.13 3 9.5 ISO Test Method 1133 ISO Test Method 527 527 85 527 80 527 3.7 527 20 178 ISO Test Method 180 179 5.5 4 179 N 100 Dry 220 65 0.85 X10-4 Dry 600 NConditioned Conditioned 600 60 2,600 Dry 5.6 Conditioned >50 20 40 Dry 160 Dry 3,000 Conditioned Conditioned 1,000
ISO Test Method 3146 75
ISO Test Method IEC 60112
BASF CorporationEngineering Plastics 1609 Biddle Avenue Wyandotte, MI 48192
General Information: 800-BC-RESIN Technical Assistance: 800-527-TECH (734-324-5150) Web address: http://www.plasticsportal.com/usa Page 1 of 2 Ultramid® B3K
Volume Resistivity Dielectric Constant (100 Hz) Dielectric Constant (1 MHz) Dissipation Factor (100 Hz) Dissipation Factor (1 MHz) UL RATINGS Flammability Rating, 1.5mm RelativeTemperature Index, 1.5mm Mechanical w/o Impact, °C Mechanical w/ Impact, °C Electrical, °C Processing Guidelines Material Handling Max. Water content:0.15% Product is supplied in sealed containers and dryingprior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 degC (176 degF) is recommended. Drying time is dependent on moisture level, but 2-4...
Ultramid® B3K
Polyamide 6
Product Description Ultramid B3K is an easy flowing, stabilized PA6 product for fast processing. Applications Typical applicationsinclude technical parts with wall thicknesses greater than 2 mm. PHYSICAL Density, g/cm³ Moisture, % (50% RH) (Saturation) RHEOLOGICAL Melt Volume Rate (275 °C/5 Kg), cc/10min. MECHANICAL Tensile Modulus,MPa 23°C Tensile stress at yield, MPa 23°C Tensile stress at break, MPa 23°C Tensile strain at yield, % 23°C Nominal strain at break, % 23°C Flexural Modulus, MPa 23°C IMPACT Izod Notched Impact, kJ/m²23°C Charpy Notched, kJ/m² 23°C -30°C Charpy Unnotched, kJ/m² 23°C -30°C THERMAL Melting Point, °C HDT A, ° C Coef. of Linear Thermal Expansion, Parallel, mm/mm °C ELECTRICAL Comparative TrackingIndex ISO Test Method 1183 62 Property Value 1.13 3 9.5 ISO Test Method 1133 ISO Test Method 527 527 85 527 80 527 3.7 527 20 178 ISO Test Method 180 179 5.5 4 179 N 100 Dry 220 65 0.85 X10-4 Dry 600 NConditioned Conditioned 600 60 2,600 Dry 5.6 Conditioned >50 20 40 Dry 160 Dry 3,000 Conditioned Conditioned 1,000
ISO Test Method 3146 75
ISO Test Method IEC 60112
BASF CorporationEngineering Plastics 1609 Biddle Avenue Wyandotte, MI 48192
General Information: 800-BC-RESIN Technical Assistance: 800-527-TECH (734-324-5150) Web address: http://www.plasticsportal.com/usa Page 1 of 2 Ultramid® B3K
Volume Resistivity Dielectric Constant (100 Hz) Dielectric Constant (1 MHz) Dissipation Factor (100 Hz) Dissipation Factor (1 MHz) UL RATINGS Flammability Rating, 1.5mm RelativeTemperature Index, 1.5mm Mechanical w/o Impact, °C Mechanical w/ Impact, °C Electrical, °C Processing Guidelines Material Handling Max. Water content:0.15% Product is supplied in sealed containers and dryingprior to molding is not required. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80 degC (176 degF) is recommended. Drying time is dependent on moisture level, but 2-4...