L. Cedeño Caero / A. Rodríguez / C. Martínez / R. Cuevas / J. Ramírez Solís
CARACTERIZACIÓN DE CATALIZADORES NIMO MODIFICADOS CON TITANIA
PARA HIDROTRATAMIENTO
Revista Mexicana de Ingeniería Química, año/vol. 2, número 001Universidad Autónoma Metropolitana - Iztapalapa
Distrito Federal, México
pp. 15-19

Red de Revistas Científicas de América Latina y el Caribe, España y Portugal
Universidad Autónoma del Estado de México

REVISTA MEXICANA DE INGENIERÍA QUÍMICA Vol. 2 (2003) 15-19

AMIDIQ

CARACTERIZACION DE CATALIZADORES NiMo MODIFICADOS CON
TITANIA PARA HIDROTRATAMIENTO
CHARACTERIZATION OF TITANIA MODIFIEDNiMo CATALYSIS FOR
HYDROTREATING
L. Cedeño-Caero*1,2, A. Rodríguez1, C. Martínez1, R. Cuevas1 y J. Ramírez-Solís1
1

2

UNICAT, Fac. de Química, UNAM. Cd. Universitaria 04510, México D.F.
Instituto Mexicano del Petróleo. Eje Central Lázaro Cárdenas No. 152 Col. San Bartolo Atepehuacan
07730, México D. F

Resumen
En el presente trabajo se presentan los resultados de la caracterización decatalizadores NiMo soportados en
alúmina modificada con diferentes contenidos de titania (3, 6 y 11% en peso). Los soportes recubiertos de titania
fueron preparados por impregnación con isopropóxido de titanio y posteriormente fluidizados con aire saturado con
vapor de agua. Se estudió el grado de reducibilidad de los catalizadores en su forma oxidada (por TPR), en su
forma sulfurada (porTPR-S) y el grado de activación por sulfuración a temperatura programada (TPS). Además,
los catalizadores fueron caracterizados por espectroscopía UV de reflectancia difusa (DRS), área específica y
distribución de tamaño de poros. Los resultados obtenidos mostraron que el catalizador de NiMo soportado sobre
alúmina recubierta con un 3% de titania, presenta la mayor cantidad de especies reducibles ypresenta una mayor
sulfuración, atribuible a una mayor cantidad de Ni octaédrico y por lo tanto, una menor pérdida en la red de la
alúmina como Ni tetraédrico.
Palabras clave: catalizadores Ni-Mo/TiO2-Al2O3, DRS, TPR, TPR-S, TPS.
Abstract
In the present work we present the results of characterization of NiMo catalysts supported on alumina covered with
variable amounts of titania (3, 6 and11 wt.%). The titania covered supports were prepared by impregnating the
alumina support with titanium isopropoxide and then fluidizing the solid sample with an air stream saturated with
water. The catalysts in their oxidic form were characterized by BET surface area, porosity, UV-vis Diffuse
Reflectance (DRS), temperature-programmed reduction (TPR) and temperature-programmed sulfiding (TPS),and
in their sulfided form by TPR-S. Sulfidation and reducibility of the catalysts were better for the catalyst supported
on alumina covered with 3 wt. % titania, in agreement with the DRS results which show an increase in the ratio of
octahedral to tetrahedral Ni. The incorporation of titania to the alumina support leads to a decrease of inactive
NiAl2O4 spinel.
Keywords: catalystsNi-Mo/TiO2-Al2O3, DRS, TPR, TPR-S, TPS.

1. Introducción
Los catalizadores más usados en la
industria de hidrotratamiento (HDT) son de
Mo soportado en alúmina con Ni o Co como
promotor, los cuales son activos en su forma
sulfurada. Durante los últimos años dadas
las drásticas restricciones ambientales, se ha
buscado que estos catalizadores sean más
activos y selectivos, lo cuál implica que
cumplancon una reducción drástica del
contenido de azufre y de aromáticos. Es

bien conocido que la modificación del
soporte puede cambiar la interacción con la
fase activa y consecuentemente la actividad
catalítica. Recientemente se ha mostrado
gran interés por la titania como soporte, dada
la mayor actividad que se obtiene para
hidrodesulfurización (HDS) de tiofeno
(Ramírez y col., 1989)...