n the experience we were checking Brinell and Vickers hardness of three different materials (aluminum, copper and bronze) by two different methods.
In the experience Brinell indenter used as a steel ball of specified diameter which load applied to the material to examine and obtain the trace left, traces left by the diameter of the sphere will allow us to obtain hardness which automaticallygives the durometer .
In the experience Vickers indenter used a square base and performs the same process in which obtained the length of the diagonals of the square footprint and left again will durometer hardness of the various materials used.
In the experience check Rockwell C hardness of three different materials (hardened steel, 1020 steel and stainless steel).
Experience Rockwell Capply a method other than the above, first we apply a preload to the material and then manually apply the durometer the rest of the load, in this experiment we used as a base cone diamond indenter hardened steel and like others applied load and give us the durometer hardness.
Keywords: Brinell, Vickers, Rockwell C, Hardness, Durometer.
1. INTRODUCCIÓN.
La dureza de un material es laresistencia que opone a la penetración de un cuerpo más duro y es una característica del material asociada a su solidez.
En el siguiente informe estaremos comprobando la dureza de 6 tipos de materiales por medio de tres métodos parecidos.
La prueba de dureza Brinell y Vickers es realizada para materiales más blandos; mientras que la dureza Rockwell C se usa para materiales mucho más duros como locomprobaremos a continuación.
2. EXPERIMENTACIÓN.
2.1 Materiales y Métodos.
Utilizamos el durómetro para aplicar la fuerza al material que son 3 bloques (bronce, cobre y aluminio) para el ensayo de dureza Brinell y Vickers, y tres cilindros pequeños (acero endurecido, acero 1020 y acero inoxidable) para el ensayo de dureza Rockwell C).
2.2 Metodología.
En el ensayo de dureza Brinellutilizamos un penetrador esférico de diámetro 2.5mm y cuadramos el durómetro para que aplique una fuerza de 187.5kg/F y de ahí obtendremos la huella circular a la cual podemos medirle el diámetro por medio del visor del durómetro y luego nos muestra la dureza del material en HB (Hardness Brinell), tomamos dos medidas por material para hallar el porcentaje de error.
En el ensayo Vickersaplicamos el mismo procedimiento anterior solo que cambiamos el penetrador esférico por uno de base cuadrada y aplicamos una fuerza de 100Kg/F y el durómetro nos da la longitud de las diagonales de la huella cuadrada dejada y luego la dureza en HV (Hardness Vickers), de los tres materiales utilizados.
En el ensayo Rockwell C en el cual usamos tres materiales diferentes (acero endurecido, acero 1020 yAcero Inoxidable) el procedimiento es diferente, primero usamos un penetrador de forma cono diamante y aplicamos una precarga manualmente al material de 10Kg/F y luego la maquina aplicara una carga de 140Kg/F para un total de 150Kg/F y luego el durómetro nos dará la dureza en HRC (Hardness Rockwell C) por medio de la cual nos es posible encontrar la profundidad de la penetración, de los tres tiposde materiales utilizados.
3. RESULTADOS Y DISCUSIONES.
3.1 Dureza Brinell.
Ø del penetrador=2.5 mm
Carga=187,5 Kg/F
d1: medida 1
d2: medida 2
D: Dureza
Material d1(mm) d2(mm) D (HB) %E
Aluminio 1.3007 1.3007 130.7 0.07
Cobre 1.5642 1.5642 86.8 0
Bronce 1.1812 1.1812 160.9 0
3.1.1 Comprobación Matemática
P: Carga; D: Diámetro esfera
d: Diámetro de marca delmaterial
h: profundidad de penetración
Material h D1 (HRC) D2 %E
Acero 1020 0.19 4.4 0
Acero Endurecido 0.15 23.4 30.7 0
Acero Inoxidable 0.14 23.3 26.1 0
HB=2P/(πD(D-√(D^2-d^2 )))
Al=(2(187.5))/(π(2.5)(2.5-√(〖(2.5)〗^2-〖(1.3007)〗^2 )))
h=(D-√(D^2-d^2 ))/2
h Al=(130.7-√(〖(130.7)〗^2-〖(1.3007)〗^2 ))/2
Aluminio = 130.8 HB h Al = 0.003 mm
Cobre = 86.8 HB h Cu =...
In the experience Brinell indenter used as a steel ball of specified diameter which load applied to the material to examine and obtain the trace left, traces left by the diameter of the sphere will allow us to obtain hardness which automaticallygives the durometer .
In the experience Vickers indenter used a square base and performs the same process in which obtained the length of the diagonals of the square footprint and left again will durometer hardness of the various materials used.
In the experience check Rockwell C hardness of three different materials (hardened steel, 1020 steel and stainless steel).
Experience Rockwell Capply a method other than the above, first we apply a preload to the material and then manually apply the durometer the rest of the load, in this experiment we used as a base cone diamond indenter hardened steel and like others applied load and give us the durometer hardness.
Keywords: Brinell, Vickers, Rockwell C, Hardness, Durometer.
1. INTRODUCCIÓN.
La dureza de un material es laresistencia que opone a la penetración de un cuerpo más duro y es una característica del material asociada a su solidez.
En el siguiente informe estaremos comprobando la dureza de 6 tipos de materiales por medio de tres métodos parecidos.
La prueba de dureza Brinell y Vickers es realizada para materiales más blandos; mientras que la dureza Rockwell C se usa para materiales mucho más duros como locomprobaremos a continuación.
2. EXPERIMENTACIÓN.
2.1 Materiales y Métodos.
Utilizamos el durómetro para aplicar la fuerza al material que son 3 bloques (bronce, cobre y aluminio) para el ensayo de dureza Brinell y Vickers, y tres cilindros pequeños (acero endurecido, acero 1020 y acero inoxidable) para el ensayo de dureza Rockwell C).
2.2 Metodología.
En el ensayo de dureza Brinellutilizamos un penetrador esférico de diámetro 2.5mm y cuadramos el durómetro para que aplique una fuerza de 187.5kg/F y de ahí obtendremos la huella circular a la cual podemos medirle el diámetro por medio del visor del durómetro y luego nos muestra la dureza del material en HB (Hardness Brinell), tomamos dos medidas por material para hallar el porcentaje de error.
En el ensayo Vickersaplicamos el mismo procedimiento anterior solo que cambiamos el penetrador esférico por uno de base cuadrada y aplicamos una fuerza de 100Kg/F y el durómetro nos da la longitud de las diagonales de la huella cuadrada dejada y luego la dureza en HV (Hardness Vickers), de los tres materiales utilizados.
En el ensayo Rockwell C en el cual usamos tres materiales diferentes (acero endurecido, acero 1020 yAcero Inoxidable) el procedimiento es diferente, primero usamos un penetrador de forma cono diamante y aplicamos una precarga manualmente al material de 10Kg/F y luego la maquina aplicara una carga de 140Kg/F para un total de 150Kg/F y luego el durómetro nos dará la dureza en HRC (Hardness Rockwell C) por medio de la cual nos es posible encontrar la profundidad de la penetración, de los tres tiposde materiales utilizados.
3. RESULTADOS Y DISCUSIONES.
3.1 Dureza Brinell.
Ø del penetrador=2.5 mm
Carga=187,5 Kg/F
d1: medida 1
d2: medida 2
D: Dureza
Material d1(mm) d2(mm) D (HB) %E
Aluminio 1.3007 1.3007 130.7 0.07
Cobre 1.5642 1.5642 86.8 0
Bronce 1.1812 1.1812 160.9 0
3.1.1 Comprobación Matemática
P: Carga; D: Diámetro esfera
d: Diámetro de marca delmaterial
h: profundidad de penetración
Material h D1 (HRC) D2 %E
Acero 1020 0.19 4.4 0
Acero Endurecido 0.15 23.4 30.7 0
Acero Inoxidable 0.14 23.3 26.1 0
HB=2P/(πD(D-√(D^2-d^2 )))
Al=(2(187.5))/(π(2.5)(2.5-√(〖(2.5)〗^2-〖(1.3007)〗^2 )))
h=(D-√(D^2-d^2 ))/2
h Al=(130.7-√(〖(130.7)〗^2-〖(1.3007)〗^2 ))/2
Aluminio = 130.8 HB h Al = 0.003 mm
Cobre = 86.8 HB h Cu =...
Leer documento completo